Product name:plastic raw material PE polyethylene virgin recycled granules pellets resins HDPE LLDPE LDPE
Color:White,transparent,customizable
TDS
| Project | Test data | Data unit | |
| Basic properties | Density | 0.921 | g/cm3 |
| Melt flow rate | 0.3 | g/10min | |
| Mechanical properties | Elongation at break | ≥450 | % |
| Tensile strength at break | ≥13 | Mpa |
| Performance | Test conditions [state] | Test method | Test data | Data unit | ||
| Basic properties | Density | ISO 1183 | 0.925 | g/cm3 | ||
| Melt flow rate | 2.16kg | ISO 1133 | 4 | g/10min | ||
| Mechanical properties | Elongation | lengthways | ISO 527 | 550 | % | |
| crosswise | ISO 527 | 700 | % | |||
| Tensile strength | lengthways | ISO 527 | 19 | MPa | ||
| crosswise | ISO 527 | 18 | MPa | |||
| Tensile strength | ISO 527 | 11 | MPa | |||
| Modulus of Elasticity | ISO 527 | 280 | MPa | |||
| Shore hardness | ISO 868 | 48 | ||||
| Fall out of strength | ASTM D-1709 | 100 | g | |||
| Thermal properties |
Vicat softening point | A/50 | ISO 306 | 94 | ºC | |
| Melting point | ISO 11357 | 112 | ºC |
| Project | Test data | Data unit | |
| Basic properties | Density | 0.9205~0.9245 | g/cm3 |
| Melt flow rate | 1.7-2.3 | g/10min | |
| Mechanical properties | Elongation at break | ≥200 | % |
| Tensile strength at break | ≥17 | Mpa | |
| Tensile strength yield | ≥3.0 | ||
| Shore hardness | ≥44 | ||
| Thermal properties |
Vicat softening point | ≥90 | ºC |
LLDPE 7149
Specification level
rotational moulding
Data sheet
| Project | Test data | Data unit | |
| Basic properties | Density | 0.935 | g/cm3 |
| Melt flow rate | 4.5-5.0 | g/10min | |
| Mechanical properties | Yield strength | ≥14 | Mpa |
| Tensile strength | ≥12 | Mpa | |
| Secant modulus | ≥340 | Mpa | |
| Embrittlement temperature | <-60 | ºC |
APPLICATIONS
Used for Barrels, cans, container,water tanks,industrial and agriculture tanks.