Platinum silicone rubber for making prosthetic body parts tattoo/exhibition
liquid silicone to make artificial hands can be use for tatoo practice, medical practice, jewelry show and so on. The FDA addition cure Silicone Rubber for life casting is nontoxic, feel like real skin and durable, good at casting ,very safe for human.
liquid silicone to make artificial hands and foot for Tattoo/exhibition is and soft, real skin liquid silicone rubber,which is suitable for molding technique with good strength, and tear strength and mixing ratio is 1:1. This is our HY-E610
liquid silicone to make artificial hands and foot for Tattoo/exhibition can also be used for producing other food grade silicone rubber products,such as orthotics prosthetics, limb, mini baby dolls, sex toys, body organs, ear, nose, mask and so om
soft liquid silicone rubber for silicone artificial hand and silicone artificial foot can not be directly used for actual production guidance. Please contact us for details.
|Mixing ratio(%)||1:1 or 10:1|
|Pot life (mins,under 25ºC)||20-40|
|Curing time (hrs,under 25ºC)||4-5(hrs under 25ºC)|
|20-30 (mins under 60ºC)|
|Hardness (Shore A)||10±2|
|Viscosity (After A/B mixed,mPa.s)||3500±1000|
|Shrinkage rate (%)||≤0.1%|
A.As it's very easy to cuase uncure problem , pls clean up all the tools which had mixed with
condensation cure silicone rubber to avoid uncure problem .
B.Do not add any pigment or powder into the addition cure silicone rubber before testing to
C.Addition cure silicone rubber is bicomponent including Part A and Part B, do not add the
Part B on the container which had hold Part A,the same for part B .
D.The mixing ratio (1:1, 10:1) must in strict accordance with the ratio in case of the changing of
1: Reach the international standard high quality with competitive price !
2: Passed the certificates including the FDA, RoHS, MSDS, SGS,ISO9001:2000 !
3: Online and on-site follow-up service for product demonstration !
4: Free technical training on products usage and operation instructions !
5: Free customer service to solve technical issues
6: Free mold opening technologies !
7: Any of our products with quality problems will be replaced within 3 months after purchase !
1, Mixing Ratio: part A: part B = 1:1/10:1
2, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes. Then the mixture could be used for pouring.
3, Please note that the thickness of the silicone affects the curing time. If the silicone used is a little thick, then the curing time will be a little longer. The temperature also affects the curing time. When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100ºC, the silicone will cure in 15 minutes; while in 25ºC room temperature, the silicone will cure around 4-5 hours.
1.The following material may hinder the curing of HY-E610, so please use after the test. If necessary, please clean the application areas.
l Organotin compound or Condensation silicone with organotin.
l Sulphur, sulfide and sulfur rubber materials.
l Amine compounds as well as contains the amine materials.
l Pewters solder flux.
2. HY-E610 should be sealed storage.
The mixture should be used up disposably to avoid causing waste.
3. HY-E610 belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix it evenly before using, which does not affect the performance.
Shenzhen Hong Ye Jie Technology Co., Ltd.
Hong Ye silicone
5,000-10,000 square meters
ISO 9000/9001/9004/19011: 2000 Others
OEM Service Offered
RTV-2 molding silicone, addition silicone,
pad printing silicone rubber, life casting silicone,
textile coating silicone rubber, liquid silicone rubber ,
manual mold silicone, LSR, trademark silicone rubber,
electronic potting silicone rubber, FDA silicone, silicon oil