The strength and toughness are excellent under proper heat treatment, and the hardness of high temperature tempering can reach 62~63HRC.
The toughness of DC53 is prominent in cold mould steel, and the tool made with DC53 seldom cracks, which greatly improves the service life.
The residual stress after wire cutting is reduced by high temperature tempering.As a result, the crack and deformation of large molds and precision molds after wire cutting are inhibited.
Advantages in line cutting
(1)Easy to be machined and grinded. The machinability and grindability are better than SKD11, so the tool life is longer and the machining time is less.
(2)The advantages of heat treatment are that the hardening capacity of quenching is higher than that of SKD11, so the defect of insufficient hardness in vacuum heat treatment can be improved.
(3) Advantages in wire cutting processing: high temperature tempering can reduce residual stress and eliminate residual austenite, preventing cracks and deformation caused by wire cutting.
(4) Advantages of surface hardening treatment: the surface hardness after surface hardening treatment is higher than that of SKD11, so the mold performance can be improved.
(5) Advantages in repairing and welding operations: since the preheating and post-heating temperatures are lower than those of SKD11, it is easier to repair and weld.Features: universal cold die steel, high hardness, high toughness DC53 die steel
1. Blanking mould, cold forming mould and cold drawing mould
2. Forming roll and punch
Piston precision stamping die.
Precision blanking die and stamping die for various purposes for wire cutting and machining.
Plastic deformation tool for refractory materials.
A die for cold forging, deep drawing and spinning.
Ending punch and stainless steel plate punch at high speed.
Our products range:
|COLD WORK STEEL|
|DC53||High Carbon High Chrome Steel||D2||SKD11||XW-5||Cr8Mo2Vsi|
|D3||COLD WORK MOLD STEEL||D3||K100||CR12|
|D2||COLD WORK MOLD STEEL||D2||SKD11/SLD||XW-41||1.2379||CR12MO1V1|
|CR12MOV||COLD WORK MOLD STEEL||CR12MOV|
|O1||OIL MOLD STEEL||O1||SK3/SK4||DF-2||1.2510||9CRWMN|
|Cr8||economic grade of Cr12|
|hot work steel|
|H13||HOT WORKING MOLD STEEL||H13||SKD61/DAC||8407||1.2344/1.2342||4CR5MOSIV1|
|FDAC||HOT WORKING MOLD STEEL||FDAC||1.2347|
|H11||HOT WORKING MOLD STEEL||H11||SKD6||1.2343|
|PLASTIC MOLD STEEL|
|P20||PLASTIC MOLD STEEL||P20||HPM7/PX88||618||1.2311||3CR2MO|
|718||PLASTIC MOLD STEEL||P20+NI||PX4/PX5||718||1.2738||3CR2NIMO|
|S136||PLASTIC MOLD STEEL||420||S-STAR||S136||1.2083||4CR13|
|NAK80||PASTIC MOLD STEEL||P21||NAK80||15NI3MN|
|HIGH SPEED STEEL|
|M2||HIGH SPEED STEEL||M2||SKH51||W6MO5CR4V2|
|M42||HIGH SPEED STEEL||M42||SKH59||W2MO9CR4VCO8|
|Alloy structural steel|
Q1: What do you do for the control of the quality?
A1: Before loading into the container, our products will all be inspected by ultrasonic inspection. Quality Grade conforms to SEP 1921-84 E/e, D/d, C/c as per customer's request.
Q2:: What are your hot-selling products ?
A2: D2/1.2379, H13/1.2344, CR12MOV, DC53, CR8, abundant stock for both plates and rounds. Competitive prices and short lead-time.
Products with this tag will be sent out within 15 days after you place an order. For the specific sending time and delivery date, please consult the supplier.
*If the supplier with the above tags do not give you the according discount or service, you can click "Contact Us" to make a complaint. If what you said is true, our professional team will help you to handle this problem.
If you are using our website on PC, you can find us by this way:
Go down to the bottom of Made-in-China.com > Go to "Help" Section> Contact Us
If you are using our Made-in-China.com App, you can find us by this way:
My Account > Click setting section which is in the top right corner > Contact Us