Application:	Refractory, Industrial Ceramic
Type:	Ceramic Plates
Color:	Yellow, White
Shape:	Round, Square, Rectangular, Cylindrical
Feature:	High Corrosion Resistance, High Fracture Toughness
Working Temperature:	1400c 1600c

Process:	Zirconia-toughened alumina ceramics, a particle size composition of the main component of alumina in the preparation of ceramic cylinder liners for drilling pumps, with an average particle size of 60-70 wt% in the range of 0.8-1.0 μm and an average particle size of 30-40 wt% of 1.0 -2.8μm range of two types of alumina. Add 15vol% of zirconia (containing 2 ~ 3mol% of yttrium oxide), add appropriate amount of dispersant, mix by ball milling, spray granulation, isostatic pressing, and fire in the temperature range of 1550 ~ 1620 C, it can be prepared for more than 2000 hours ceramic cylinder liner,and the forming and firing yield is high, and the raw material and process costs are low. The performance of zirconia-toughened alumina ceramics is better than 99 alumina ceramics, and the price is much lower than that of zirconia ceramics.Many occasions where alumina ceramics are incompetent show a better performance-price ratio than zirconia ceramics.
Components	80% al2o3,20% zro2
Application:	Standoffs,Insulators,Probe Bodies,Pump Components,Bushings,Pump Piston Sleeves,Instrument,Sensor Bulbs,Valve Seals,Impellers,Fluid Delivery System Components,Analytical Instrument Column
Shapes:	Plate and cylindrical (can also be customized according to drawings).
Advantages:	High Corrosion Resistance,High Corrosion Resistance,High Fracture Toughness,Lower Cost Than Zirconia,High Erosion Resistance

Density	g/cm3	4.2
Water absorption	%	0
Sintering temperature	C	1650
Hardness	HV(Gpa)	1650
Bending strength	Mpa	500~600
Compressive strength	Mpa	2800
Rupture strength	Mpa.m3/2	9.8
Modulus of elasticity	Gpa	310
Max temperature	C	1500
Coefficient of thermal expansion	/C	8.2*10-6
Thermal conductivity	W/m.k(25-300C)	9.8

Zirconia Toughened Alumina Ceramic Zta Rods for Mould