| Customized: | Non-Customized |
|---|---|
| Standard: | JIS |
| Length: | Taper-length |
| Type: | Core Drill Bit |
| Material: | Tungsten Carbide |
| Usage: | Well Drilling, Masonry Drilling |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Tungsten carbide tip product performance:
1,high hardness and wear resistance, especially at a high temperature still has a high hardness;
2,high elastic modulus, high bending strength;
4,relatively stable chemical property, acid, alkali resistance, even at high temperature does not occur obvious oxidation.
Tungsten carbide tip application range:
Mainly used for mining, stone processing, safety hammer head, litchi surface cutter head.
Safety hammer tip Tungsten carbide tip: tungsten carbide safety hammer tip than alloy steel material higher hardness, better toughness, longer service life, the tip is not easy to passivation, breaking speed.
Safety hammer tip tungsten carbide head main specifications and sizes are D3*5, D3*7, D4*8, D4.6*8.0, D4.6*8.5 and so on; Complete range, head can be sharpened, can be customized production, welcome to inquire!
Lychee surface stone processing: high hardness tungsten carbide tip can be used to beat stones, make marble lychee surface, stone breaking fast, high purity tungsten carbide head long service life.
The main specifications of tungsten carbide head for stone beating are: D4*8, D4.6*8, D4.6*8.5, D4.6*9, D8*10, etc., which can be customized according to requirements.
| Grade | YG8 |
| Tungsten carbide | 8%co 92%wc |
| Density | 14.74g/cm3 |
| Hardness | 89.5hra |
| TRS | 2710MPa |
| Sizes | dia.4.6*8.0mm |
| Grade |
CO+WC (%) |
Density (g/cm3) |
Hardness (hra) |
TRS (MPa) |
| YG6 | 6%CO 94%WC | 14.95 | 89.5 | 2580 |
| YG8 | 8%CO 92%WC | 14.74 | 89 | 2710 |
| YG6X | 6%CO 94%WC | 14.93 | 91 | 2480 |