Bonding Function: | Structural Adhesive |
---|---|
Morphology: | Water Emulsion |
Application: | Automobile, Construction, Woodworking, Fiber & Garment, Packing, Wood Making Glue |
Material: | PVA |
Classification: | Room Curing |
Main Agent Composition: | Natural Polymer |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
PRODUCT DESCRIPTION
Main Component
|
VAM ,PVAC , CAE
|
Viscosity
|
50000- 80000mpa.s
|
Appearance
|
Light yellow emulsion
|
Solidifying Time
|
(20°C)90- 120min
|
Solid Content
|
38%-48%
|
Compression Shear
Strength(Dry)
|
≥ 11.2MpaPH Value
|
PH Value
|
5-8
|
Compression Shear
Strength(Wet)
|
≥ 4.5Mpa
|
Suggested Amount for
Application
|
150-200g/m2
|
Proportion of
Hardener
|
8%-12%
|
Water
Resistance
|
The adhered boards keep stable after immersing in 102°C boiled water for 8 hours. The adhered boards also keep stable after immersing in water in normal temperature for 240 hours |