Standard: | JIS, GB, ASTM |
---|---|
Application: | Loader, Construction Machinery, Metallurgical Machinery, Cement Plant, Mining Machine, Thermal Power Plant, Coal Yard |
Material: | Alumina Ceramics |
Type: | Wear Resistant Ceramic |
Item: | Alumina Ceramic Tile Liner |
Application Industry: | Industrial Ceramic,Mining,Power Plant,Steel Plant, |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Alumina ceramic tile popular Sizes (Length*width*thickness ) |
100*100*20mm (4"x4"x3/4") |
150*100*13mm (6"x4"x1/2") |
150*100*15mm (6"x4"x5/8") |
150*100*20mm (6"x4"x3/4") |
150*100*25mm (6"x4"x1") |
150*100*50mm (6"x4"x2") |
150*50*25mm (6"x4"x1") |
100*75*25mm (4"x3"x1") |
120*80*20mm |
228*114*25mm |
114*114*25mm |
More sizes and customized size acceptable. Chemshun ceramics afford the relative weldable steel cone and ceramic rod. |
Item | content |
Alumina content | 92% |
Density | ≥ 3.62g/cm3 |
Abrasion loss | 0.014cm3/10minutes |
Rockwell A hardness | ≥87 HRA |
Moh' s hardness | 9 grade |
impact strength | ≥850 Mpa |
bending strength | ≥ 290 Mpa |
thermal conductivity | 20 W/m.K |
thermal expansion coefficent | 7.2*10(-6)/m.K |
water absorption | none |
surface | smooth, clear, pure white |
size | normal size and custom-design can be supplied |
No. |
Item |
Data |
ZTA ceramics property |
||
1 |
ZrO2 |
20-25% |
2 |
Al2O3 |
75-80% |
3 |
Density(g/cm3) |
≥4.2 |
4 |
Compressive Strength(Mpa) |
≥1500 |
5 |
Vickers Hardness (HV 10) |
≥1300 |
6 |
Rockwell hardness (HRA) |
≥90 |
7 |
Flexural Strength (20ºC, Mpa) |
>350 |
8 |
Elastic Modulus(Gpa) |
320 |
9 |
Fracture Toughness KIC (Mpa.m1/2) |
≥3.70 |
Rubber Property |
||
10 |
Rubber |
Natural |
11 |
Tensile strength (Mpa) |
>12 |
12 |
Tensile Elongation |
>400% |
13 |
Hardness (Shore A) |
55~65 |
14 |
Bond strength of rubber and ceramics (shear modulus, Mpa) |
>3.5 |