| CAS No.: | / |
|---|---|
| Formula: | / |
| EINECS: | / |
| Color: | Orange Grey |
| Appearance: | Liquid |
| Main Raw Material: | Epoxy |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Resin Type | Waterborne modified epoxy resin Modified polyamine curing agent |
| Gloss | Semi gloss (25 ~ 35%) |
| Viscosity of original paint (rotary viscometer, 64# rotor, 60rpm, 25ºC) | Component A: 2000-2500mps; Component B: 500-1000mps |
| Proportion (g/ml) | Component A: 1.41±0.05; Component B: 1.05±0.03 |
| Mass solid content (105ºC×3h) | 60±2% |
| Volumetric solid content | 41±3% |
| Recommended dry film thickness | 90-120µm |
| VOC | ≤80g/L |
| Mixing proportion | Main agent: curing agent = 12:1 (weight ratio); Main agent: curing agent = 8.9:1 (volume ratio) |
| Storage life | 6 months |
| Test Item | Result | |
| Drying time (temperature: 25ºC, humidity: 80% RH) |
Surface dry time: 1h; Ultimate dry time: 24h |
Fully cured in 7 days |
| Using drier: 40-80ºC×20min~40min | ||
| Adhesive(1mm,grade) | 1 | |
| Pencil hardness | HB | |
| Impact (50cm) | Pass | |
| Flexibility | 2mm | |
| Neutral salt spray resistance | 360-600h | |
| Water resistance (normal temperature deionized water) | 1000h | |
| Composition | Component A & B |
| Mix proportion | 12:1 (Weight ratio) |
| Mix method | After mixing component A, add component B and fully mix evenly |
| Diluent | Deionized water |
| Curing period(25ºC) | 15-20min |
| Pot-life(25ºC) | 2h |
| Pretreatment of substrate | The substrate shall be polished and make sure to be clean, dry, rust-free, oil-free, etc. |
| Construction viscosity | 7500-8800mPa.s(25ºC) |