TYPICAL APPLICATIONS |
for pressure pipe, for gas and water distribution, sewage and drainage. | ||
| Physical | Method | Unit | Value |
| Density | ISO 1183 | g/cm3 | 0.959 |
| Melt Flow Rate (190°C /5kg) | ISO 1133 | g/10 min | 0.23 |
| Melt Flow Rate (190°C /21.6kg) | ISO 1133 | g/10 min | 6.4 |
| Staudinger Index Jg | ISO 1628 | Ml/g | 380 |
| Vicat Softening Temperature(VST/B/50 K/h (50N)) | ISO 306 | °C | 74 |
| Mechanical | Mechod | Unit | Value |
| Tensile Modulus (23°C, v = 1mm/min, Secant) | ISO 527-1, -2 | MPa | 900 |
| Tensile Stress @ Yield (23°C, v = 50 mm/min) | ISO 527-1, -2 | MPa | 23 |
| Tensile Strain @ Yield (23°C, v = 50 mm/min) | ISO 527-1, -2 | % | 9 |
| Tensile Creep Modulus 1h [Test stress in MPa] | ISO 899-1 | MPa | 850 [2.0] |
| Tensile Creep Modulus 1000h [Test stress in MPa] | ISO 899-1 | MPa | 360 [2.0] |
| Maximum Elongation TD | EN 638 | % | >350 |
| MRS Classification | ISO/TR 9080 | MPa | 10 |
| Flexural Stress at 3,5% deflection | ISO 178 | MPa | 21 |
| FNCT (4.0 MPa, 2% Arkopal N 100, 80°C) | ISO 16770 | h | >1000 |
| Flexural Creep Modulus (4 Point loading method, 1 min-value) (4 Point loading method, 24 h-value) (4 Point loading method, 2000 h-value) |
DIN 19537-2 |
MPa MPa MPa |
1100 560 330 |
| Charpy Notched Impact Strength (23°C) (-30°C) |
ISO 179 | kJ/m2 kJ/m2 |
26 13 |
| Shore Hardness (Shore D (3 sec)) | ISO 868 | 63 | |
| Oxidation Induction Time (OIT) (210°C) | EN 728 | min | 30 |
| Carbon Black Content | ISO 6964 | % | 2.25 |
| Odour Treshold | EN1622/EN1240 | <2 | |