Application: | Electrical Winding Insulation, Motor |
---|---|
Type: | Solid |
Chemistry: | Inorganic Insulation |
Material: | Glass Fiber |
Thermal Rating: | H 180 |
Maximum Voltage: | <10KV |
Customization: |
---|
Suppliers with verified business licenses
H200-W | H200-G-W | F150-G-W | |||
Thermal class | H | F | |||
Volatile content | % | not above : 2 | |||
Loss of weight at calcination | % | 26±2 | |||
Soluble resin content | % | above : 90 | |||
Tensile strength before curing | N/cm | above:2000 | above :1500 | above :1000 | |
Maximum pull while banding | N/cm | 1000 | 800 | 800 | |
Tensilestrength of ringlike sample at room temperature after curing | Mpa | 200c | |||
above :1000 | above :900 | above :900 | |||
Tensile strength of ringlike sample at working temperature after curing | Mpa | 2000c | 1800c | 1500c | |
above :700 | above :600 | above :560 | |||
Proof tracking index | above 500V | ||||
Arc resistance | S | above : 160 | |||
Breakdown voltage parallel to layers | KV | normal condition:adove 25 after soaked in water for 24 hours:above 10 |
|||
Thermosetting | OK | ||||
Loss of tensile strength after soaked in oil | not above:10% | ||||