Uses | Automotive Electrical | Consumer Industria Hydrocarbon and Energy |
||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.16 g/cm³ 1.16 |
ISO 1183 ASTM D792 |
||
Moisture Absorption | ISO 62-4 | |||
23 °C;50% RH/24hrs | 0.15 % | |||
23 °C;50% RH/Equilibrium | 0.3 % | |||
Water Absorption | ||||
24 hrs;23 °C | 0.7 % | ISO 62-1 | ||
23 °C;saturated | 3.5 % | ISO 62-1 | ||
24 hrs;23 °C | 0.7 % | ASTM D570 | ||
23°C/Saturated | 3.5 % | ASTM D570 | ||
Melt Volume Rate, MVR | ISO 1133 | |||
2.16 kg;MVR at 250 °C | 5 cm³/10 min | |||
5 kg;MVR at 250 °C | 15 cm³/10 min | |||
5 kg;MVR at 260 °C | 23 cm³/10 min | |||
Melt Flow Rate[MFR](250 °C;5 kgf) | 15 g/10min | ASTM D1238 | ||
Mold Shrinkage, Flow | 0.5 - 0.7 % | Method | ||
Mold Shrinkage, XFlow | 0.6 - 0.8 % | Method | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 80*10*4;23 °C 80*10*4;-30 °C 23 °C -30 °C |
60 kJ/m² 60 kJ/m² 850 J/m 750 J/m |
ISO 180/1A ISO 180/1A ASTM D256 ASTM D256 |
||
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
65 kJ/m² 65 kJ/m² |
ISO 180/1A | ||
Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | ||
Izod Impact, Unnotched 80*10*4;23 °C 80*10*4;-30 °C 23 °C -30 °C |
NB kJ/m² NB kJ/m² NB J/m NB J/m |
ISO 180/1U ISO 180/1U ASTM D4812 ASTM D4812 |
||
C harpy Impact, V-Notched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
60 kJ/m² 60 kJ/m² |
ISO 179 1eA | ||
C harpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp =62 mm 0 -30 °C;Edgew;80*10*4;sp =62 mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU | ||
Multi-Axial Instrumented Impact, Total Energy 23 °C -30 °C |
65 J 65 J |
ISO 6603-2 | ||
Multi-Axial Instrumented Impact, Peak Energy 23 °C -30 °C |
55 J 55 J |
ISO 6603-2 | ||
Instrumented Dart Impact, Total Energy 23 °C -30 °C |
40 J 40 J |
ASTM D3763 | ||
Instrumented Dart Impact, Energy at Peak 23 °C -30 °C |
35 J 35 J |
ASTM D3763 | ||
Instrumented Dart Impact, Peak force 23 °C -30 °C |
4000 N 4800 N |
ASTM D3763 | ||
Tensile Modulus | ||||
1 mm/min | 1750 MPa | ISO 527 | ||
50 mm/min | 1750 MPa | ASTM D638 | ||
Tensile Stress, Yield | ||||
50 mm/min | 45 MPa | ISO 527 | ||
50 mm/min;Type I | 45 MPa | ASTM D638 | ||
Tensile Strain, Yield | ||||
50 mm/min | 5.5 % | ISO 527 | ||
50 mm/min;Type I | 5.5 % | ASTM D638 | ||
Tensile Strain, Break | ||||
50 mm/min | > 60 % | ISO 527 | ||
50 mm/min;Type I | > 60 % | ASTM D638 | ||
Tensile Nominal Strain, Break | ||||
50 mm/min | > 60 % | ISO 527 | ||
50 mm/min;Type I | > 60 % | ASTM D638 | ||
Flexural Modulus | ||||
2 mm/min | 1825 MPa | ISO 178 | ||
1.3 mm/min;50 mm;span | 1900 MPa | ASTM D790 | ||
Flexural Strength | ||||
2 mm/min | 70 MPa | ISO 178 | ||
1.3 mm/min;50 mm;span | 70 MPa | ASTM D790 | ||
Ball Indentation Hardness(H358/30) | 78 MPa | ISO 2039-1 | ||
Thermal | Nominal Value | Test Method | ||
HDT/Af(1.8) | 105 °C | ISO 75/Af | ||
HDT/Bf(0.45) | 123 °C | ISO 75/Bf | ||
Vicat Softening Temperature | ||||
Rate B/50 | 123 °C | ISO 306 | ||
Rate B/120 | 123 °C | ISO 306 | ||
Rate A/50 | 137 °C | ISO 306 | ||
Rate A/120 | 138 °C | ISO 306 | ||
Rate B/50 | 123 °C | ASTM D1525 | ||
Rate B/120 | 123 °C | ASTM D1525 | ||
CTE, Flow | ||||
23°C to 50°C | 8.5E-05 1/°C | ISO 11359-2 | ||
23°C to 50°C | 8.5E-05 1/°C | ASTM E831 | ||
CTE, XFlow | ||||
23°C to 50°C | 1.1E-04 1/°C | ISO 11359-2 | ||
23°C to 50°C | 1.1E-04 1/°C | ASTM E831 | ||
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm |
105 °C 123 °C |
ASTM D648 | ||
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | ||
Electrical | Nominal Value | Test Method | ||
Comparative Tracking Index | 175 V | IEC 60112 | ||
Surface Resistivity, ROA | 1.0E+09 - 1.0E+11 ohms | IEC 60093 | ||
Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B | ||
Dielectric Constant(6.0e+10 - 9.0e+10 Hz) | 2.73 | |||
Dissipation Factor(6.0e+10 - 9.0e+10 Hz) | 0.022 | |||
Surface Resistivity | 1.0E+09 - 1.0E+11 ohms | ASTM D257 |