Steel grit
|
|
Chemical Composition
|
C
|
0.70~1.20%
|
|
|
Mn
|
0.35~1.20%
|
|
|
Si
|
≥0.40%
|
|
|
S
|
MAX 0.02
|
|
|
P
|
MAX 0.02
|
|
Microhardness
|
Normal:40~50HRC (377~509HV) Special:52~56HRC (543~620HV) Special:56~60HRC (620~713HV)
|
|
|
Hardness Deviation
|
Max Deviation ±3.0HRC
|
|
|
Microstructure
|
Tempered martensite or tempered troostite
|
|
|
Density
|
7.4g/m³
|
|
|
Product
|
Steel shot , Steel grit , Cut wire shot ,etc
|
|
Size
|
Steel shot : S70,S110,S130,S170,S230,S280,S330,S390,S460,S550,S660,S780,S930,etc
Steel grit : G14,G16,G18,G25,G40,G50,G80,G120,etc
Cut wire shot : 0.5mm,1.0mm,1.5mm,2.0mm ,etc
|
|
Standard
|
EN12413, ISO9001:2008
|
|
Micro structure
|
Tempered Martensite or Sorbite
|
|
Hardness
|
HRC 40-65
|
|
Field
|
Cement plant , Mining , Power station , Chemical industries ,etc
|
|
MOQ
|
1 ton
|
|
Lead Time
|
In 15 days for quantity under 100 tons
|
|
Testing
|
Size testing ,Hardness testing ,Chemical composition testing
|
|
Free Sample
|
Available upon request
|
Product Feature
Technical Specification
Available Size: S110, S170, S230, S280, S330, S390, S460, S550, S660, S780
| Item | Technique data | |
|
Chemical composition |
C | 0.10-0.20% |
| Si | 0.10-0.35% | |
| Mn | 0.35-1.50% | |
| S | ≤0.05% | |
| P | ≤0.05% | |
| Other alloy elements | Cr,Mo, Ni, B, Al, Cu etc | |
| Hardness | HRC40-54 | |
| Microstructure | Martensite and Bainise duplex structure | |
| Item | Technique data | Remarks | |
| Chemical Compostion | C | 0.10%-0.20% | Sulphur and Phosphorus are the harmful elements,should be reduced in order to decrease the friability and increase the fatigue life |
| Si | 0.10%-0.35% | ||
| Mn | 0.35%-1.50% | ||
| S | ≤0.05% | ||
| P | ≤0.05% | ||
| other alloy elements | adding Cr Mo Ni B Al Cu etc alloy elements | adding alloy elements make it have the excellent property of alloy steel | |
| Hardness | HRC42-48/48-52 | the proper hardness insure the efficiency of surface treatment | |
| Microstructure | Martensite and Bainise duplex structure | duplex structure can ensure high tenacity and high strength | |