Riginal High Density Polyethylene Granules HDPE

CAS No.:	9002-88-4
Formula:	C2h4on
EINECS:	618-339-3
Environmental Protection:	Yes
Color:	White
Kind:	HDPE Resin

Customization:	Available \| Customized Request

Contact Supplier

Contact Now

Inquiry Basket

Shengzhou Worthside Chemical Co., Ltd.

Gold Member Since 2020

Suppliers with verified business licenses

Zhejiang, China

Audited Supplier

Importers and Exporters

The supplier has import and export rights

High Repeat Buyers Choice

More than 50% of buyers repeatedly choose the supplier

Years of Export Experience

The export experience of the supplier is more than 10 years

Experienced Team

The supplier has 6 foreign trading staff(s) and 6 staff(s) with over 6 years of overseas trading experience

to see all verified strength labels (11)

Product Description

Company Info.

Basic Info.

Model NO.

s-1000

Appearance

Granulars

Transport Package

25kg

Specification

99.9

Origin

China

Production Capacity

500 Mt a Month

Product Description

Product Description:
HDPE is a white powder or granular product. Non-toxic, tasteless, crystallinity was 80% ~ 90%, softening point is 125 l ~ 35 ºC, using temperature is 100 ºC; Hardness, tensile strength and creep are better than low density polyethylene. Good wear resistance, electrical insulation, toughness and cold resistance; Good chemical stability, at room temperature, insoluble in any organic solvents, acid, alkali and various kinds of salt corrosion resistance; The film has little permeability to water vapor and air and low water absorption. Aging resistance, environmental stress cracking resistance is better than low density polyethylene, especially hot oxidation will make its performance degradation, so must be added in the resin antioxidant and uv absorber, etc to improve the deficiency of. The heat deformation temperature of high density polyethylene film is low under stress.

Specification :

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.946-0.952	g/cm3
MFR	5kg	ISO 1133	0.15-0.45	g/10min
Tensile strength at yield		ISO 527-2	21min	MPa
Elongation at break		ISO 527-2	300min	%
Tensile modulus		GB/T 1040.2-2006	1000	mpa
vicat softening point		ASTM D-1525	126	°C
thermal stability		GB/T 19466	20min	min