Usage: | Concrete, Filling Material |
---|---|
Material: | 100% Polyester |
Feature: | Anti-Pilling |
Fiber Type: | Staple |
Pattern: | Hollow Conjugated Silicon |
Color: | White |
Customization: |
---|
Suppliers with verified business licenses
regenerated 1.4D 1.5D 3D 6D 7D 15D black polyester staple fiber
Brand Name |
Square |
Commodity |
Recycled Polyester Staple Fiber |
Grade |
Recycled AAA,Recycled AA,Recycled A |
Made From |
Pet Flakes,Color Master Batch,Toner,Pop Corn |
Denier |
1.4D-30D |
Cut Length |
25mm-102mm |
Color |
All Colors |
Application |
Spinning,Non-Woven Fabric,Carpet/Rug,Filling |
recycled polyester staple fiber
Specifications
Size: 1.2d to 15D
Cut length: 32 - 102mm
Abnormal fibre: ≤50mg/100g
Oil pick up: 0.11 - 0.15%
Tenacity: 3.8 to 5.0cn/dtex
Annual Capacity: 50000 tons
Our recycled polyester staple fiber is made from our self-produced masterbatches.
We can produce fiber based on your specific requirements.
We guarantee the best color and most reliable quality products.
If you are interested in this recycled polyester staple fiber, please feel free to contact Alice.
we always expect long-term and mutual benefit business relationships with you from all over the world. Look forward to cooperating with you soon!
Polyester FibersGeotextiles |
Performance of geotextile is commonly termed "durability" when it is used to making roads, pools and used in constructions. due to the good strengthern of our recycled solid non siliconsied fiber, the fabric's durability could be increased and give us a long life |
ITEM |
UNIT |
Middle volume |
Tolerances |
Titer |
DENIER |
7 |
±25 % |
Fiber Length |
MM |
64 |
±10% |
Crimper count |
count/25mm |
15-17 |
10±4 |
Double-length fiber |
mg/100g |
0 |
≤200 |
Contents of defect |
mg/100g |
0 |
≤400 |
Puff V1 |
cm3/g |
166 |
≥155 |
Puff V2 |
cm3/g |
65 |
≥50 |
Puff V3 |
cm3/g |
146 |
≥160 |
Hollowness |
% |
20 |
±12% |
Specific resistance |
Ω·cm |
2.93X109 |
≤1010 |
Elasticity Recovery |
% |
60 |
≥58 |
ITEM |
UNIT |
Middle volume |
Tolerances |
Titer |
DENIER |
3 |
±25 % |
Fiber Length |
MM |
64 |
±10% |
Crimper count |
count/25mm |
14-16 |
10±4 |
Double-length fiber |
mg/100g |
0 |
≤200 |
Contents of defect |
mg/100g |
22 |
≤400 |
Puff V1 |
cm3/g |
176 |
≥155 |
Puff V2 |
cm3/g |
58 |
≥50 |
Puff V3 |
cm3/g |
151 |
≥160 |
Hollowness |
% |
20 |
±12% |
Specific resistance |
Ω·cm |
6.76x107 |
≤1010 |
Elasticity Recovery |
% |
60 |
≥58 |
Virgin Grade |
|||
White Hollow conjugated Silicon | White Hollow conjugated Silicon | ||
&Non-silicon polyester Grade A | &Non-silicon polyester Regular | ||
6D,7D15d(32mm,51mm,64mm) | 6D,7D15d(32mm,51mm,64mm) |
Polyester Staple Fiber(HCS)/6.67dtex×64mm(32mm) |
||||
Test project | For value | |||
linear density(dtex) | 6.67 | |||
Deviation rate of linear density, % | 15 | |||
length (mm) | 64 | |||
Deviation rate of length , % | -1 | |||
Number of roll, per 25mm | 8.6 | |||
Hollow ratio, % | 22.2 | |||
filling power V1,cm3/g | 164 | |||
filling power V2,cm3/g | 44 | |||
oil content, % | 80 | |||
Over-cut fiber content, mg/100g | 4 | |||
Defect content,mg/100mg | 10 | |||
Moisture,% | 0.4 | |||
Slippery degrees | 3.5 |