| Refractoriness (℃): | 1580< Refractoriness< 1770 |
|---|---|
| Feature: | Long Time Materials |
| Type: | Refractory Material |
| Shape: | Grain |
| Material: | Castable |
| Size: | According to The Requirement |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
| Index/Brand | WAM-T80 | WAM-T90 | WAM-T100 | WAM-T110 | |
| Safety application temp C | 800 |
900 |
1000 |
1100 |
|
| AL2O3 ≥ % | 26 | 28 | 32 | 35 | |
| Bulk density | 110 CX24h | 0.5 | 0.7 | 0.9 | 1.0 |
≤ g/cm 3 |
800 C x3h 0.48 |
900 C x3h 0.67 |
1000 C x3h 0.86 |
1100 C x3h 0.9 |
|
| Bending strength | 110 Cx24h | - | 0.6 | 1.3 | 1.5 |
| 815 C x3h | - | - | 0.8 | 1.0 | |
≥ MPa |
- | 900 C x3h 0.5 |
1000 C x3h 0.8 |
110 C x3h 1.2 |
|
| Crushing strength | 110 C x24h | 0.7 | 1.5 | 3.5 | 4.5 |
| 815 C x3h | - | - | 3.0 | 3.0 | |
≥ MPa |
800 C x3h 0.6 |
900 C x3h 1.0 |
1000 C x3h 3.0 |
1100 C x3h 3.5 |
|
| Linear change | 815 C X3h | - | - | -0.5 | -0.4 |
≤ % |
800 C x3h -0.8 |
900 C x3h -0.4 |
1000 C x3h -0.6 |
1100 C x3h -0.7 |
|
| Thermal conductivity (350± 25 C ) ≤ W/m. k | 0.17 |
0.20 |
0.23 |
0.24 |
|
| Water addition % | 74-77 | 47-50 | 33-36 | 32-35 | |
| installation | Coating, Casting | Coating, Casting | Casting, gunning | Casting, gunning | |
Applications |
Used as insulating lining, sealing and filling materials for kilns and furnaces of many kinds | Used as double insulating lining for catalytic cracking devices and used as insulating lining for tuyere pipe and heating furnace lining in chemical industry | Used as double insulating lining for catalytic cracking devices and used as insulating lining for tuyere pipe flue pipe and heating furnace lining in chemical industry | Used as double insulating lining for drum part and accessory part of catalytic cracking devices, and as heating furnace lining in chemical industry | |