Properties
|
Test Condition
|
Test Method
|
Unit
|
Typical Value
|
|
Physical
|
|
|||
|
Specific Gravity
|
|
ASTM D792
|
-
|
1.21
|
|
Molding Shrinkage (Flow), 3.2mm
|
|
ASTM D955
|
%
|
0.5 ~ 0.7
|
|
Melt Flow Rate
|
300ºC/1.2kg
|
ASTM D1238
|
g/10min
|
12
|
|
Mechanical
|
|
|||
|
Tensile Strength, 3.2mm
|
|
ASTM D638
|
|
|
|
@ Yield
|
50mm/min
|
|
kg/cm^2
|
630
|
|
Tensile Elongation, 3.2mm
|
|
ASTM D638
|
|
|
|
@ Yield
|
50mm/min
|
|
%
|
|
|
@ Break
|
50mm/min
|
|
%
|
100
|
|
Tensile Modulus, 3.2mm
|
1mm/min kg/cm^2
|
ASTM D638
|
kg/cm^2
|
|
|
Flexural Strength, 3.2mm
|
10mm/min
|
ASTM D790
|
kg/cm^2
|
970
|
|
Flexural Modulus, 3.2mm
|
10mm/min
|
ASTM D790
|
kg/cm^2
|
23,000
|
|
IZOD Impact Strength, 3.2mm
|
|
ASTM D256
|
|
|
|
(Notched)
|
23ºC
|
|
kg·cm/cm
|
70
|
|
|
-30ºC
|
|
kg·cm/cm
|
|
|
Rockwell Hardness
|
R-Scale
|
ASTM D785
|
-
|
118
|
|
Thermal
|
|
|||
|
Heat Deflection Temperature, 6.4mm
|
|
ASTM D648
|
|
|
|
(Unannealed)
|
18.6kg
|
|
ºC
|
130
|
|
|
4.6kg
|
|
ºC
|
|
|
Vicat Softening Temperature
|
|
ASTM D1525
|
|
|
|
|
5kg, 50ºC/h
|
|
ºC
|
140
|
|
Ball Pressure Temperature
|
|
IEC 60695-10-2
|
ºC
|
|
|
Burning Rate,3.2mm
|
|
FMVSS 302
|
mm
|
|
|
Flammability
|
|
UL94
|
|
|
|
1.0mm
|
|
|
class
|
V-0
|
|
1.5mm
|
|
|
class
|
V-0
|
|
1.7mm
|
|
|
class
|
V-0,5VB
|
|
3.0mm
|
|
|
class
|
V-0,5VA
|
|
Relative Temperature Index
|
|
UL 746B
|
|
|
|
Electrical
|
|
|
ºC
|
125
|
|
Mechanical with Impact
|
|
|
ºC
|
120
|
|
Mechanical without Impact
|
|
|
ºC
|
125
|
|
Electrical
|
|
|||
|
Comparative Tracking Index(CTI)
|
Solution A
|
IEC 60112
|
Volts
|
|
|
Surface Resistivity
|
|
IEC 60093
|
Ohm
|
|
|
Volume Resistivity
|
23ºC
|
ASTM D257
|
Ohm·m
|
|
|
Arc Resistance
|
23ºC
|
ASTM D495
|
Ohm·cm
|
|
|
Dielectric Strength, 1mm
|
23ºC
|
ASTM D149
|
kV/mm
|
|
|
Dielectric Constant (10^6 Hz)
|
23ºC
|
ASTM D150
|
sec
|
|