| CAS No.: | - |
|---|---|
| Formula: | Mixture |
| EINECS: | - |
| Bonding Function: | Structural Adhesive |
| Morphology: | Solid-State |
| Application: | Construction |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
|
Before curing
|
Curing system
|
De-alcoholized
|
|
Visual appearance
|
Slightly flowing paste
|
|
|
Color
|
White
|
|
|
Specific gravity, g/cm3
|
2.60
|
|
|
Curing
|
The curing process starts once the product is exposed to the vapour content in the air | |
|
Surface drying time, in minutes
|
<5
|
|
|
Film curing (finger sensible), in minutes
|
<5 | |
|
Curing speed (at 23ºCand relative humidity of 50%)
|
||
|
Within 48 hours, in mm
|
>5
|
|
|
Application temperature (ºC)
|
5~40
|
|
| Cured |
Specific gravity, g/cm3
|
2.61
|
|
Hardness (Shore A)
|
88 | |
|
Applicable range of temperature (ºC)
|
-5~200
|
|
|
Mechanical property after 3 days of curing (at 23ºC & RH50%)
|
||
|
Tensile strength, MPa
|
4.4 | |
|
Permittivity kV/mm
|
19 | |
|
Volumetric resistivity (Ω.cm)
|
10 16
|
|
|
Breaking elongation rate, %
|
12 | |
|
Flame retardant grade
|
UL94V0
|
|
|
Thermal conductivity (W/mK)
|
1.5 | |