Audited Supplier Product Description 50% Glass Reinforced PA4T Heat Stabilized for Automotive
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
| Product Description | ||
| 50% Glass Reinforced, PA4T, Heat Stabilized, for Automotive applications | ||
| General | ||
| Form Resin Pellets | ||
| Filler 50 % Glass Fiber | ||
| Feature Good Thermal | ||
| Uses Automotive | ||
| Physical Nominal Value Test Method | ||
| Density, dry 1.66 g/cm³ ISO 1183 | ||
| Condition: Density 1.64 g/cm³ ISO 1183 | ||
| Dry: Molding Shrinkage, Across Flow 0.90 % ISO 294-4 | ||
| Dry: Molding Shrinkage, Flow 0.35 % ISO 294-4 | ||
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.3 % ISO 62 | ||
| Mechanical Nominal Value Test Method | ||
| Dry: Tensile Modulus ISO 527-2 | ||
| 18000 MPa | ||
| -40 °C 18500 MPa | ||
| 40 °C 17500 MPa | ||
| 80 °C 17300 MPa | ||
| 100 °C 17000 MPa | ||
| 120 °C 16000 MPa | ||
| 150 °C 11500 MPa | ||
| 160 °C 10000 MPa | ||
| 180 °C 8000 MPa | ||
| 200 °C 7200 MPa | ||
| Condition: Tensile Modulus 18000 MPa ISO 527-2 | ||
| Dry: Tensile Stress, Break -40 °C 40 °C 80 °C 100 °C 120 °C 150 °C 160 °C 180 °C 200 °C |
250 MPa 300 MPa 235 MPa 205 MPa 190 MPa 170 MPa 130 MPa 120 MPa 100 MPa 85.0 MPa |
ISO 527-2 |
| Condition: Tensile Stress, Break | 250 MPa | ISO 527-2 |
| Dry: Tensile Strain, Break -40 °C 40 °C 80 °C 100 °C 120 °C 150 °C 160 °C 180 °C 200 °C |
2.0 % 2.3 % 2.0 % 2.0 % 2.1 % 2.1 % 3.4 % 4.1 % 4.9 % 5.0 % |
ISO 527-2 |
| Condition: Tensile Strain, Break | 2.0 % | ISO 527-2 |
| Dry: Flexural Modulus 120 °C 160 °C 180 °C 200 °C |
17200 MPa 15700 MPa 10000 MPa 8000 MPa 7400 MPa |
ISO 178 |
| Dry: Flexural Stress | 370 MPa | ISO 178 |
| Dry: Charpy Notched Impact Strength -30 °C 23 °C |
13 kJ/m² 12 kJ/m² |
ISO 179 1eA |
| Condition: Charpy Notched Impact Strength(23 °C) | 12 kJ/m² | ISO 179 1eA |
| Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
75 kJ/m² 80 kJ/m² |
ISO 179 1eU |
| Condition: Charpy Unnotched Impact Strength(23 °C) | 80 kJ/m² | ISO 179 1eU |
| Thermal | Nominal Value | Test Method |
| Dry: Heat Deflection Temperature, Unannealed(1.8 MPa) | 320 °C | ISO 75-2/A |
| Dry: Melting Temperature(10 °C/min) | 335 °C | ISO 11357-3 |
| Dry: CLTE, Flow | 2.7E-5 cm/cm/°C 1.5E-5 cm/cm/°C |
ASTM D696 ISO 11359-2 |
| Dry: CLTE, Transverse | 3.0E-5 cm/cm/°C 5.0E-5 cm/cm/°C |
ASTM D696 ISO 11359-2 |