Audited Supplier LEXAN 505RU Polycarbonate (PC) is an injection moldable non-chlorinated/brominated flame retardant grade that is 10% glass fiber filled. It It is UV stabilized and has a UL94 [email protected] rating and is available in various opaque color options. This is an alternative to LEXAN 503R, 503R, 503RS.
| Tensile Elongation, Break 5 mm/min;Type I |
6.0 % 6.0 % |
ASTM D638 ISO 527-2/5 |
| Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min |
3200 MPa 3500 MPa |
ASTM D790 ISO 178 |
| Flexural Stress, at Yield(2 mm/min) | 122 MPa | ISO 178 |
| Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 114 MPa | ASTM D790 |
| Charpy Notched Impact Strength -30 °C;80 23 °C;80 |
7.0 kJ/m² 10 kJ/m² |
ISO 179 1eA |
| Charpy Unnotched Impact Strength -30 °C;80 23 °C;80 |
No Break No Break |
ISO 179 1eU |
| Notched Izod Impact -30 °C 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
70 J/m 90 J/m 8.0 kJ/m² 10 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
| Unnotched Izod Impact 23 °C -30 °C;80*10*3 mm 23 °C;80*10*3 mm |
1200 J/m 73 kJ/m² No Break |
ASTM D4812 ISO 180/1U ISO 180/1U |
| Instrumented Dart Impact, Total Energy(23 °C) | 25.0 J | ASTM D3763 |
| Thermal | Nominal Value | Test Method |
| Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span |
137 °C 136 °C |
ASTM D648 ASTM D1525 |
| Vicat Softening Temperature | ||
| 50 °C/h;50 N;Rate A;Loading 2 | 149 °C 147 °C |
ISO 306 ISO 306/B50 |
| Ball Pressure Test(123 - 127 °C) | Pass | ISO 11359-2 |
| CLTE, Flow(-40 - 40 °C) | 5.0E-5 cm/cm/°C | ASTM E831 |
| CLTE, Transverse -40 - 40 °C -40 °C |
7.4E-5 cm/cm/°C 8.5E-5 cm/cm/°C |
ASTM E831 ISO 11359-2 |
| Flame Rating, Testing by SABIC 0.75 mm 1.5 mm 3 mm 3 mm |
V-2 V-0 5VA 5VB |
UL 94 |
| Glow Wire Flammability Index(0.75 mm) | 960 °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
850 °C 875 °C |
IEC 60695-2-13 |
| Electrical | Nominal Value | Test Method |
| Comparative Tracking Index[CTI] | PLC 3 | UL 746 |
| Comparative Tracking Index | 175 V | IEC 60112 |
| High Amp Arc Ignition, HAI, Surface | PLC 0 | UL 746 |
| Hot-wire Ignition, HWI | PLC 3 | UL 746 |
| Processing | Nominal Value |
| Drying Temperature<Injection> | 120 °C |
| Drying Time<Injection> | 2.0 - 4.0 hr |
| Suggested Max Moisture<Injection> | 0.020 % |
| Hopper Temperature<Injection> | 60 - 80 °C |
| Rear Temperature<Injection> | 270 - 300 °C |
| Middle Temperature<injection> | 280 - 310 °C |
| Front Temperature<Injection> | 290 - 320 °C |
| Nozzle Temperature<Injection> | 280 - 310 °C |
| Processing Temp, Melt<Injection> | 290 - 320 °C |
| Mold Temperature<Injection> | 80 - 120 °C |