Audited Supplier | Product Description | ||||||||
| LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non- brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is UV stabilized(F1 rating) providing additional weathering capability. LUX7632C is available in diffusion colors. |
||||||||
| General | ||||||||
| Form | Resin Pellets | |||||||
Feature |
F1 | Non-Brominated & Non- Chlorinated Flame Retardant |
Non-Chlorinated Diffusive |
|||||
| UL Yellow Card | E207780-101256997 | |||||||
| Uses Lighting Diffusers Consumer Electrical | ||||||||
| Physical | Nominal Value | Test Method | ||||||
| Density / Specific Gravity | 1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 |
||||||
| Mold Shrinkage, Flow(3.2 mm) | 0.55 - 0.75 % | SABIC Method | ||||||
| Mold Shrinkage, XFlow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | ||||||
| Melt Flow Rate[MFR](300 °C;1.2 kgf) | 5 g/10min | ASTM D1238 | ||||||
| Water Absorption(23 °C;saturated) | 0.14 % | ISO 62-1 | ||||||
| Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | ||||||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 5 cm³/10 min | ISO 1133 | ||||||
| UV light, water exposure/immersion | f1 | UL 746C | ||||||
| Mechanical | Nominal Value | Test Method | ||||||
| Izod Impact, Unnotched | ASTM D4812 | |||||||
| 23 °C | NB J/m | |||||||
| -30 °C | NB J/m | |||||||
| Izod Impact, Notched | ASTM D256 | |||||||
| 23 °C | 100 J/m | |||||||
| -30 °C | 85 J/m | |||||||
| Instrumented Dart Impact, Total Energy(23 °C) | 66 J | ASTM D3763 | ||||||
| Unnotched Izod Impact Strength | ISO 180/1U | |||||||
| unnotched;80*10*3;23 °C 0 | NB kJ/m² | |||||||
| unnotched;80*10*3;-30 °C 0 | NB kJ/m² | |||||||
| Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A | ||||||
| C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
10 kJ/m² 9 kJ/m² |
ISO 179 1eA | ||||||
| C harpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU | ||||||
| Tensile Stress, Yield | ||||||||
| 50 mm/min;Type I | 68 MPa | ASTM D638 | ||||||
| 50 mm/min | 67 MPa | ISO 527 | ||||||
| Tensile Stress, Break | ||||||||
| 50 mm/min;Type I | 52 MPa | ASTM D638 | ||||||
| 50 mm/min | 52 MPa | ISO 527 | ||||||
| Tensile Strain, Yield | ||||||||
| 50 mm/min;Type I | 6 % | ASTM D638 | ||||||
| 50 mm/min | 6 % | ISO 527 | ||||||
| Tensile Strain, Break | ||||||||
| 50 mm/min;Type I | 51 % | ASTM D638 | ||||||
| 50 mm/min | 23 % | ISO 527 | ||||||
| Tensile Modulus | ||||||||
| 50 mm/min | 2500 MPa | ASTM D638 | ||||||
| 1 mm/min | 2400 MPa | ISO 527 | ||||||
| Flexural Stress, Yield | ||||||||
| 1.3 mm/min;50 mm;span | 106 MPa | ASTM D790 | ||||||
| 2 mm/min | 103 MPa | ISO 178 | ||||||
| Flexural Modulus | ||||||||
| 1.3 mm/min;50 mm;span | 2400 MPa | ASTM D790 | ||||||
| 2 mm/min | 2500 MPa | ISO 178 | ||||||
| Thermal | Nominal Value | Test Method | ||||||
| UL Recognized ≥ 3 mm ≥ 1 mm ≥ 0.4 mm |
5VA V-0 V-2 |
UL 94 | ||||||
| Glow Wire Ignition Temperature [GWIT] 3 mm 1 mm |
850 °C 875 °C |
IEC 60695-2-13 | ||||||
| Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C |
IEC 60695-2-12 | ||||||
| Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 137 °C 139 °C |
ASTM D1525 ISO 306 ISO 306 |
||||||
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
131 °C 120 °C |
ASTM D648 | ||||||
| CTE, Flow -40 - 40 °C 23°C to 80°C |
6.6E-05 1/°C 7.2e-05 1/°C |
ASTM E831 ISO 11359-2 |
||||||
| CTE, XFlow -40 - 40 °C 23°C to 80°C |
7.0E-05 1/°C 7.6E-05 1/°C |
ASTM E831 ISO 11359-2 |
||||||
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 | ||||||
| HDT/Be(Edgew;120*10*4;sp =100mm; 0.45 Mpa) | 131 °C | ISO 75/Be | ||||||
| Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp =100mm) | 120 °C | ISO 75/Ae | ||||||
| Relative Temp Index, Elec | 125 °C | UL 746B | ||||||
| Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B | ||||||
| Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B | ||||||
| Electrical | Nominal Value | Test Method |
| Dielectric Constant, Dk(1.1e+9 Hz) | 2.79 | ASTM ES 7-83 |
| Dissipation Factor, Df(1.1e+9 Hz) | 5.8E-03 | ASTM ES 7-83 |
| Comparative Tracking Index, CTI | PLC 3 | UL 746A |
| Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm |
PLC 2 PLC 3 |
UL 746A |
| High Amp Arc Ignition, HAI( ≥ 1 mm) | PLC 0 | UL 746A |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Drying Time, Cumulative<Injection> | 48 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 290 - 310 °C | |
| Nozzle Temperature<Injection> | 280 - 305 °C | |
| Front, Zone 3 Temperature<Injection> | 290 - 310 °C | |
| Middle, Zone 2 Temperature<Injection> | 275 - 300 °C | |
| Rear, Zone 1 Temperature<Injection> | 265 - 290 °C | |
| Mold Temperature<Injection> | 70 - 95 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed <Injection> | 40 - 70 rpm | |
| Shot To Cylinder Size<Injection> | 40 - 60 % | |
| Vent Depth <Injection> | 0.025 - 0.076 mm |