Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | ||||||
Nonhalogenated. 3.5 MFR. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Chlorinated Flame R t d t | ||||||
UL Yellow Card E45587-236867 | ||||||
Lighting Applications Constraction |
||||||
Physical Nominal Value Test Method | ||||||
Density / Specific Gravity 1.19 - 1.20 g/cm³ ASTM D792 | ||||||
Specific Volume 0.830 cm³/g ASTM D792 | ||||||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 3.5 g/10min ASTM D1238 | ||||||
Molding Shrinkage, Flow(3.2 mm) 0.50 - 0.70 % Internal Method | ||||||
Water Absorption(24 hr) 0.15 % ASTM D570 | ||||||
Water Absorption, Equilibrium ASTM D570 | ||||||
23 °C 0.35 % | ||||||
100 °C 0.58 % | ||||||
Outdoor Suitability f2 UL 746C | ||||||
Rockwell Hardness, M-Scale 70 ASTM D785 | ||||||
Rockwell Hardness, R-Scale 118 ASTM D785 | ||||||
Mechanical Nominal Value | Test Method | |||||
Tensile Strength, Yield(50 mm/min;Type I) 62.0 MPa | ASTM D638 | |||||
Tensile Strength, Break(50 mm/min;Type I) 65.0 MPa | ASTM D638 | |||||
Tensile Elongation, Yield(50 mm/min;Type I) 7.0 % | ASTM D638 | |||||
Tensile Elongation, Break(50 mm/min;Type I) 110 % | ASTM D638 | |||||
Flexural Modulus(1.3 mm/min;50 mm;Span) 2340 MPa | ASTM D790 | |||||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 93.0 MPa | ASTM D790 | |||||
Taber Abrasion Resistance(1.0e+3 Cycles;1.0e+3 g;CS-1710.0 mg Wheel) |
ASTM D1044 | |||||
Notched Izod Impact(23 °C) 910 J/m | ASTM D256 | |||||
Unnotched Izod Impact(23 °C) 3200 J/m | ASTM D4812 | |||||
Gardner Impact(23 °C) 169 J | ASTM D3029 | |||||
Tensile Impact Strength(Type S) 546 kJ/m² | ASTM D1822 | |||||
Thermal Nominal Value | Test Method | |||||
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;6.4 mm |
137 °C 132 °C |
ASTM D648 | ||||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 154 °C | ASTM D1525 | ||||
CLTE, Flow(-40 - 95 °C) 6.8E-5 cm/cm/°C | ASTM E831 | |||||
Specific Heat 1250 J/kg/°C | ASTM C351 | |||||
Thermal Conductivity 0.19 W/m-K | ASTM C177 | |||||
RTI Elec 125 °C | UL 746 | |||||
RTI Imp 115 °C | UL 746 | |||||
RTI Str 125 °C | UL 746 | |||||
Flame Rating(1.5 mm) HB | UL 94 | |||||
Electrical | Nominal Value | Test Method | ||||
Volume Resistivity | > 1.0E+17 ohms ·cm | ASTM D257 | ||||
Dielectric Strength, in Air(3.2 mm) | 15 kV/mm | ASTM D149 | ||||
Dielectric Constant 60 Hz 5.0e+4 Hz 1.0e+6 Hz |
3.17 3.17 2.96 |
ASTM D150 | ||||
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
9.0E-4 9.0E-4 0.010 |
ASTM D150 | ||||
Comparative Tracking Index, CTI | PLC 2 | UL 746 | ||||
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 | ||||
High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746 | ||||
Hot-wire Ignition, HWI | PLC 2 | UL 746 | ||||
Optical | Nominal Value | Test Method | ||||
Refractive Index | 1.586 | ASTM D542 | ||||
Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 | ||||
Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 | ||||
Processing | Nominal Value | |||||
Drying Temperature<Injection> | 120 °C | |||||
Drying Time<Injection> | 3.0 - 4.0 hr | |||||
Suggested Max Moisture<Injection> | 0.020 % | |||||
Suggested Shot Size<Injection> | 40 - 60 % | |||||
Rear Temperature<Injection> | 300 - 320 °C | |||||
Middle Temperature<injection> | 310 - 330 °C | |||||
Front Temperature<Injection> | 320 - 345 °C | |||||
Nozzle Temperature<Injection> | 315 - 340 °C | |||||
Processing Temp, Melt<Injection> | 320 - 345 °C | |||||
Mold Temperature<Injection> | 80 - 115 °C | |||||
Back Pressure<Injection> | 0.300 - 0.700 MPa | |||||
Screw Speed <Injection> | 40 - 70 rpm | |||||
Vent Depth <Injection> | 0.025 - 0.076 mm | |||||
Drying Time, Cumulative<Injection> | 48 hrs |