| Material: | Polyvinyl Chloride/PVC |
|---|---|
| Usage: | General Plastics, Specialty Plastics |
| Color: | Customized |
| Application: | Insulated and Sheathing Cable |
| Density: | 1.35-1.55g/Cm³ |
| Hardness: | 65-90 Shore a |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Type&Specification
|
Technical specifications of 70 ºC PVC compound |
||
|
Tensile strength |
MPa |
20.5 |
|
Fracture tensile strain |
% |
320 |
|
Ageing temperature |
ºC |
100 |
|
Ageing time |
h |
168 |
|
Tensile strength after ageing |
MPa |
22.5 |
|
Max change of tensile strength |
% |
12 |
|
After ageing fracture tensile strain |
% |
290 |
|
Max change of fracture tensile strain |
% |
-10 |
|
Thermal deformation |
% |
28 |
|
Thermal ageing quality loss |
g/m2 |
19 |
|
200ºC thermal stability time |
min |
90 |
|
20ºC volume resistivity |
Ω.cm |
2.0*1011 |
|
Technical specifications of 90 ºC PVC compound |
||
|
Tensile strength |
MPa |
20 |
|
Fracture tensile strain |
% |
330 |
|
Ageing temperature |
ºC |
100 |
|
Ageing time |
h |
240 |
|
Tensile strength after ageing |
MPa |
21.5 |
|
Max change of tensile strength |
% |
8 |
|
After ageing fracture tensile strain |
% |
310 |
|
Max change of fracture tensile strain |
% |
-6 |
|
Thermal deformation |
% |
28 |
|
Thermal ageing quality loss |
g/m2 |
9 |
|
200ºC thermal stability time |
min |
120 |
|
20ºC volume resistivity |
Ω.cm |
2.0*1010 |
Application:
Hard and transparent PVC granules for shrink film, extrusion pipes and profile,IC electronic acknowledge tubes, shelf labels of supermarket, retaining strips of shower room, screwdriver handle, packing boxes.
(1) High transparency, good cloth and weathering resistance
(2) With a high bending resistance strength and excellent thermal stability, which can be produced continuously for a long time.
(3) Easy to print and without any printing defect points.