| CAS No.: | 9009-54-5 |
|---|---|
| Formula: | C3h8n2o |
| EINECS: | 210-898-8 |
| Molecular Principal Chain: | Carbon Chain Polymer |
| Color: | White |
| Application: | for Make Shoe Sole |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Name of products Nombre de productos |
@40ºC Appearance Apariencia |
Density (g/cm3 @40oC) Densidad |
Viscosity (mPa·s @40oC) Viscosidad |
Package Size (kg/drum) Dimensiones del embalaje |
| HD-4160-3(POL, A) | Liquid Líquido |
1.13~1.18 | 800~1050 | 18 / 220 |
| HD-2122T(ISO, B) | Liquid Líquido |
1.18~1.20 | 250~350 | 20 / 235 |
| HD-4160-3 (POL, A, Poliol) | Hardener/g Endurecedor/g |
water/g Agua/g |
catalyst/g Catalizador/g |
other otro |
| 18 kg(one drum/un envase) | 0 | 50~110 | 260 | It depends /Dependiendo |
| 220 kg (one drum/un envase) | 0 | 600~1300 | 3200 | It depends/Dependiendo |
Test Items Ítem de prueba |
Reactivity parameters Parámetros técnicos |
Test Items Ítem de prueba |
Product performance Propiedades del Producto |
Ratio of (A+C) and B material Proporción de (Poliol+C) y Iso |
100/105~110 | Moulding density(g/cm3) Densidad de Moldeo(g/cm3) |
0.28~0.33 |
Material temperature (oC) Temperatura de Material (oC) |
40~45/38~42 | Hardness(23ºC) Dureza |
55C~75C 40A~60A |
Cream time (s) Tiempo de crema (s) |
4~6 | Tensile strength(MPa) Resistencia del estiramiento (MPa) |
≥4 |
End of rise time (s) Tiempo de fin del subida (s) |
15~25 | Elongation(%) Alargamiento(%) |
≥350 |
Free rise density (g/cm3) Densidad de subida libre (g/cm3) |
0.14~0.22 | Tear strength(kN/m) Fuerza de desgarro(kN/m) |
≥13 |
Metal mold temperature (oC) Temperatura de molde metal (oC) |
45~55 | Flexing resistance(23ºC) Resistencia de Plegado(23ºC) |
4 40,000 times no crack 40,000 veces no grietas |
Demould time(min) Tiempo de demoldar (min) |
2~2.5 | DIN DIN abrasion resistance(mm3) Resistencia de la abrasión(mm3) |
≤450 |
Suppliers with verified business licenses
Audited Supplier 