Product Description | |||
Hostaform® LW15EWX is a specialty low wear grade of acetal copolymer designed for improved performance including when paired against other thermoplastic resins (PBT, PA, PC, PMMA) or steel. Due to the special wax blend the material has a good weld line strength. Compared to Hostaform® LW90EWX this grade has higher toughness and strength. | |||
General | |||
Form | Resin Pellets | ||
Feature | Ductile | Abrasion Resistant | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.40 g/cm³ | ISO 1183 | |
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 2.5 cm³/10 min | ISO 1133 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2650 MPa | ISO 527-2/1A | |
Tensile Stress, Yield | 63.0 MPa | ISO 527-2/1A/50 | |
Tensile Strain, Yield | 19 % | ISO 527-2/1A/50 | |
Nominal Tensile Strain at Break | 32 % | ISO 527-2/1A/50 | |
Charpy Notched Impact Strength | ISO 179 1eA | ||
-30 °C | 11 kJ/m² | ||
23 °C | 14 kJ/m² | ||
Thermal | Nominal Value | Test Method | |
Heat Deflection Temperature, Unannealed(1.8 MPa) | 93.0 °C | ISO 75-2/A | |
Melting Point(10 °C/min) | 173 °C | ISO 11357-3 |
Product Description | ||||
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
General | ||||
Form | Resin | Pellets | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.40 g/cm³ | |||
Water Absorption | 0.21 % | ASTM D570 | ||
Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
Linear Mold Shrinkage | 2.2 % | |||
Linear Mold Shrinkage, Transverse | 1.8 % | |||
Hardness, Rockwell R | 111 | ASTM D785 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
Elongation at Break | 30 % | ASTM D638 | ||
Flexural Strength | 52.0 MPa | ASTM D790 | ||
Flexural Modulus | 2100 MPa | ASTM D790 | ||
Compressive Strength | 66.0 MPa | ASTM D695 | ||
Shear Strength | 40.0 MPa | ASTM D732 | ||
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
Flammability, UL94 | HB | UL 94 |