| Feature: | Plastics |
|---|---|
| CAS No.: | 25766-59-0 |
| Formula: | C6h4c(CH3)2c6h4oco2-]N |
| Samples: |
25kg/bag
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier | Product Description | |||||
| PC 30x-15 Applications: Appliances,Storage media housings, Business equipment, Electrical & lighting components,Transportation,Automotive applications, Houseware, Recreation, Packaging applications, Power equipment Characteristics: 30x-15 MFR are general purpose Polycarbonate resins that offer exceptional impact resistance, heat distortion resistance and optical clarity typically used in injection moulding. The CALIBRE 300-15 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer. Material is transparent but can be custom colored. Govt. and Industry Standards:Underwriters Laboratory, Inc. (UL) |
|||||
| General | |||||
| Form | Resin Pellets | ||||
| Clear/Transparent Good Thermal Clean/High Purity | |||||
| Feature | Improved Impact R i t |
||||
| es s ance | |||||
| Appliances Lighting Applications Business Equipment | |||||
| Uses | Packaging Electrical |
Automotive Electric equipments |
Household Applications Mass Transportation | ||
| Energy Storage | |||||
| Physical Nominal Value Test Method | |||||
| Density / Specific Gravity 1.20 g/cm³ | ASTM D792;ISO 1183 | ||||
| Melt Flow Rate[MFR](300 ºC;1.2 kg) 15 g/10min | ASTM D1238;ISO 1133 | ||||
| Mold Shrinkage, Flow 0.50 - 0.70 % ISO 294-4 | |||||
| Water Absorption at Saturation(23 °C) 0.32 % ISO 62 | |||||
| Water Absorption at Equilibrium(23 °C;50 %RH) 0.12 % ISO 62 | |||||
| Rockwell Hardness M-Scale(23 °C) 73 ASTM D785 | |||||
| Rockwell Hardness R-Scale(23 °C;50 %RH) 118 ASTM D785 | |||||
| Mechanical | Nominal Value | Test Method | |||
| Tensile Modulus | |||||
| 1 mm/min | 2300 MPa 2300 MPa |
ASTM D638 ISO 527-1/1 |
|||
| Tensile Strength, Yield | |||||
| 50 mm/min | 60.0 MPa 60.0 MPa |
ASTM D638 ISO 527-2/50 |
|||
| Tensile Strength, Break | |||||
| 50 mm/min | 71.0 MPa 71.0 MPa |
ASTM D638 ISO 527-2/50 |
|||
| Elongation at Yield | |||||
| 50 mm/min | 6.0 % 6.0 % |
ASTM D638 ISO 527-2/50 |
|||
| Elongation at Break | |||||
| 50 mm/min | 130 % 130 % |
ASTM D638 ISO 527-2/50 |
|||
| Flexural Modulus | 2410 MPa |
ASTM D790 |
|||
| 2 mm/min | 2400 MPa | ISO 178 | |||
| Flexural Strength | 96.5 MPa |
ASTM D790 |
|||
| 2 mm/min | 97.0 MPa | ISO 178 | |||
| C harpy Notched Impact Strength -30 °C 23 °C |
12 kJ/m² 25 kJ/m² |
ISO 179/1eA | |||
| Izod Impact, Notched | |||||
| 23 °C | 850 J/m | ASTM D256 | |||
| 23 °C | 83 kJ/m² | ISO 180/1A | |||
| Instrumented Dart Impact, Total Energy(23 °C;3.33 m/sec) | 87.0 J | ASTM D3763 | |||
| Tensile Impact Strength | 462 kJ/m² | ASTM D1822 | |||
| Thermal | Nominal Value | Test Method | |||
| Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa 1.8 MPa |
138 °C 127 °C 124 °C |
ASTM D648 ASTM D648 ISO 75-2/A |
|||
| Deflection Temperature Under Load, Annealed 0.45 MPa 1.8 MPa |
143 °C 140 °C |
ISO 75-2/B;ASTM D648 ISO 75-2/A;ASTM D648 |
|||
| Vicat Softening Temperature(50 °C/h;50 N) | 148 °C | ISO 306/B50;ASTM D1525 5 | |||
| Ball Indentation Temperature | > 125 °C | IEC 60335-1 | |||
| CLTE, Flow(-40 - 80°C) | 6.8E-5 cm/cm/°C | ISO 11359-2 | |||
| Flame Rating 1.5 mm 3 mm 3 mm 0.75 mm 1.5 mm |
HB HB HB V-2 V-2 |
UL 94 | |||
| Glow Wire Flammability Index 1 mm 2 mm 3 mm |
900 °C 875 °C 875 °C |
IEC 60695-2-12 | |||
| Glow Wire Ignition Temperature [GWIT] 1 mm 2 mm 3 mm |
800 °C 775 °C 775 °C |
IEC 60695-2-13 | |||
| Oxygen Index | 26 % | ISO 4589-2 | |||
| Electrical | Nominal Value | Test Method | |||
| Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 | |||
| Dielectric Strength | 17 kV/mm 17 kV/mm |
ASTM D149 IEC 60243-1 |
|||
| Relative Permittivity 100 Hz 1.0e+6 Hz |
3.00 3.00 |
IEC 60250 | |||
| Dissipation Factor 50 Hz 1.0e+6 Hz |
1.0E-3 2.0E-3 |
ASTM D150 | |||
| Comparative Tracking Index, Solution A(2 mm) | 250 V | IEC 60112 | |||
| Optical | Nominal Value | Test Method | |||
| Refractive Index | 1.586 | ISO 489 | |||
| Transmittance (3.0e+3 µm) | 87.0 - 91.0 % | ASTM D1003 | |||
| Haze | < 1.00 % | ASTM D1003 | |||
| Processing | Nominal Value | ||||
| Drying Temperature | 120 °C | ||||
| Drying Time | 4.0 hr | ||||