| 30% Glass Reinforced, High Flow, Halogen free and free of red phosphorous | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 30 % Glass Fiber | ||
| Red Phosphorous Free Feature |
Non-Brominated & Non- Excellent Processability Chlorinated Flame | ||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity | 1.43 g/cm³ | ISO 1183 | |
| Spiral Flow, Injection Pressure 1 mm;800 bar 1 mm;1.0e+3 bar 1 mm;1.2e+3 bar |
8.70 cm 10.4 cm 12.1 cm |
||
| Molding Shrinkage, Across Flow | 1.3 % | ISO 294-4 | |
| Molding Shrinkage, Flow | 0.28 % | ISO 294-4 | |
| Water Absorption(24 hr;23 °C) | 1.0 % | ISO 62 | |
| Water Absorption, Saturation(23 °C) | 4.9 % | ISO 62 | |
| Water Absorption, Equilibrium(50% RH;23 °C) 1.6 % ISO 62 | |||
| Mechanical | Nominal Value | Test Method |
| Tensile Modulus 1 mm -40 °C 100 °C 120 °C 140 °C 160 °C |
11000 MPa 11000 MPa 1130 MPa 5800 MPa 5300 MPa 4800 MPa 4600 MPa |
ISO 527-2 |
| Tensile Stress, Break 1 mm -40 °C 100 °C 120 °C 140 °C 160 °C |
150 MPa 140 MPa 200 MPa 87.0 MPa 79.0 MPa 72.0 MPa 66.0 MPa |
ISO 527-2 |
| Tensile Strain, Break 1 mm -40 °C 120 °C 140 °C 160 °C |
2.8 % 2.6 % 3.0 % 5.4 % 5.7 % 6.0 % |
ISO 527-2 |
| Flexural Modulus | 9450 MPa | ISO 178 |
| Flexural Stress | 225 MPa | ISO 178 |
| Charpy Notched Impact Strength(23 °C) | 10 kJ/m² | ISO 179 1eA |
| Charpy Unnotched Impact Strength(23 °C) | 68 kJ/m² | ISO 179 1eU |
| Thermal | Nominal Value | Test Method |
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 247 °C | ISO 75-2/A |
| Glass Transition Temperature(10 °C/min) | 60.0 °C | ISO 11357-2 |
| Ball Pressure Test(255 °C) | Pass | IEC 60695-10-2 |
| CLTE, Flow | 2.1E-5 cm/cm/°C | ISO 11359-2 |
| CLTE, Transverse(0.75 mm) | 6.7E-5 cm/cm/°C | ISO 11359-2 |
| Flammability Classification 3 mm |
V-0 V-0 |
IEC 60695-11-10, - 20 |
| Glow Wire Flammability Index 0.4 mm 3 mm |
960 °C 960 °C |
IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT] 0.4 mm 3 mm |
800 °C 825 °C |
IEC 60695-2-13 |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 |
| Electric Strength | 41 kV/mm | IEC 60243-1 |
| Relative Permittivity 100 Hz 1.0e+6 Hz 1.0e+9 Hz |
4.24 3.87 3.60 |
IEC 60250 |
| Dissipation Factor 100 Hz 1.0e+6 Hz 1.0e+9 Hz |
0.011 0.015 0.010 |
IEC 60250 |
| Comparative Tracking Index | 600 V | IEC 60112 |
| Processing | Nominal Value | |
| Melting Point(10 °C/min) | 260 °C |