Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html30% Glass Reinforced, High Flow
Product Description | |||||
30% Glass Reinforced, High Flow | |||||
General | |||||
Form | |||||
Filler | |||||
Feature | Excellent Processability | ||||
UL Yellow Card E47960-271796 | |||||
Phys | ical | Nominal Value | Test Method | ||
Dry: | Density | 1.35 g/cm³ | ISO 1183 | ||
Dry: | Molding Shrinkage, Across Flow | 0.86 % | ISO 294-4 | ||
Dry: | Molding Shrinkage, Flow | 0.18 % | ISO 294-4 | ||
Dry: | Water Absorption, Saturation(23 °C) | 6.0 % | ISO 62 | ||
Dry: | Water Absorption, Equilibrium(50% RH;23 °C) | 1.8 % | ISO 62 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 9350 MPa | ISO 527-2 |
Condition: Tensile Modulus | 5700 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 160 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 105 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 |
Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 |
Dry: Flexural Modulus | 8500 MPa | ISO 178 |
Dry: Flexural Stress | 235 MPa | ISO 178 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
10 kJ/m² 12 kJ/m² |
ISO 179 1eA |
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
10 kJ/m² 22 kJ/m² |
ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
65 kJ/m² 85 kJ/m² |
ISO 179 1eU |
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
65 kJ/m² 90 kJ/m² |
ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
220 °C 200 °C |
ISO 75-2/B ISO 75-2/A |
Dry: Melting Temperature(10 °C/min) | 220 °C | ISO 11357-3 |
Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
Dry: CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
Dry: Flammability Classification(1.6 mm) | HB | IEC 60695-11-10, - 20 |
Electrical | Nominal Value | Test Method |
Condition: Surface resistivity | 1.0E+14 ohms | IEC 60093 |
Dry: Volume Resistivity | 1.0e+15 ohms·cm | IEC 60093 |
Condition: Volume resistivity | 1.0E+13 ohms·cm | IEC 60093 |
Dry: Relative permittivity 100 Hz 1000000 Hz |
3.50 3.30 |
IEC 60250 |
Condition: Relative Permittivity 100 Hz 1000000 Hz |
14.0 5.00 |
IEC 60250 |
Dry: Dissipation Factor 100 Hz 1000000 Hz |
5.0E-3 0.015 |
IEC 60250 |
Condition: Dissipation factor 100 Hz 1000000 Hz |
0.30 0.12 |
IEC 60250 |
Condition: Comparative Tracking Index | 600 V | IEC 60112 |