30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-conducting nylon
Product Description | ||||
30% Glass Reinforced, PA4T, High Flow, Halogen free and free of red phosphorous | ||||
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Feature |
Red Phosphorous Free | Non-Brominated & Non- Excellent Processability Chlorinated Flame | ||
UL Yellow Card E47960-101041561 | ||||
Physical | Nominal Value | Test Method | ||
Density, dry | 1.46 g/cm³ | ISO 1183 | ||
Dry: Molding Shrinkage, Across Flow | 1.1 % | ISO 294-4 | ||
Dry: Molding Shrinkage, Flow | 0.30 % | ISO 294-4 | ||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.8 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Dry: Tensile Modulus | 11000 MPa | ISO 527-2 | ||
Condition: Tensile Modulus | 11000 MPa | ISO 527-2 | ||
Dry: Tensile Stress, Break | 140 MPa | ISO 527-2 | ||
Condition: Tensile Stress, Break | 135 MPa | ISO 527-2 | ||
Dry: Tensile Strain, Break | 1.9 % | ISO 527-2 | ||
Condition: Tensile Strain, Break | 1.8 % | ISO 527-2 | ||
Dry: Flexural Modulus | 10500 MPa | ISO 178 | ||
Condition: Flexural Modulus | 10500 MPa | ISO 178 | ||
Dry: Flexural Stress | 210 MPa | ISO 178 | ||
Condition: Flexural Stress | 200 MPa | ISO 178 | ||
Dry: Charpy Notched Impact Strength(23 °C) | 8.0 kJ/m² | ISO 179 1eA | ||
Condition: Charpy Notched Impact Strength(23 °C) | 8.0 kJ/m² | ISO 179 1eA | ||
Dry: Charpy Unnotched Impact Strength(23 °C) | 40 kJ/m² | ISO 179 1eU | ||
Condition: Charpy Unnotched Impact Strength(23 °C) | 40 kJ/m² | ISO 179 1eU | ||
Thermal | Nominal Value | Test Method | ||
Dry: Heat Deflection Temperature, Unannealed(1.8 MPa) | 295 °C | ISO 75-2/A | ||
Dry: Melting Temperature(10 °C/min) | 325 °C | ISO 11357-3 | ||
Dry: CLTE, Flow | 3.0E-5 cm/cm/°C 2.1E-5 cm/cm/°C |
ASTM D696 ISO 11359-2 |
||
Dry: CLTE, Transverse | 5.0E-5 cm/cm/°C 6.5E-5 cm/cm/°C |
ASTM D696 ISO 11359-2 |
||
Dry: RTI Elec(0.35 mm) | 140 °C | UL 746 | ||
Dry: Flammability Classification 0.4 mm 1.5 mm |
V-0 V-0 |
IEC 60695-11-10, - 20 | ||
Electrical | Nominal Value | Test Method | ||
Dry: Volume Resistivity | > 1.0E+15 Ohms ·cm | IEC 60093 | ||
Condition: Volume resistivity | 1.0e+15 ohms ·cm | IEC 60093 | ||
Dry: Relative permittivity 100 Hz 1.0e+6 Hz 1.0e+9 Hz |
4.40 4.10 3.90 |
IEC 60250 | ||
Condition: Relative Permittivity 100 Hz 1.0e+6 Hz |
5.30 4.30 |
IEC 60250 | ||
Dry: Comparative Tracking Index | 600 V | IEC 60112 |