Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Nylon 6 Per kg Price pa66 Pellets Polyamide 6 66 Gf30 Pa Resin Granules Flame Retardant Fr v0 Gf20% Pa6 Nylon With Glass Fiberhttps://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html30% Glass Reinforced, Heat Stabilized, High FlowInformation provided by DSM
Product Description | ||||
30% Glass Reinforced, Heat Stabilized, High FlowInformation provided by DSM | ||||
General | ||||
Resin Pellets | ||||
30 % Glass Fiber | ||||
Physical | Nominal Value | Test Method | ||
Density | 1.35 g/cm³ | ISO 1183 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Break | 105 MPa | ISO 527-1/2 | ||
Elongation at Break | 7.00 % | ISO 527-1/2 | ||
Tensile Modulus | 5700 MPa | ISO 527-1/2 | ||
Charpy Impact Unnotched Temperature; -30 °C Temperature; 23 °C | 65 kJ/m² 90 kJ/m² |
ISO 179 1eU | ||
Charpy Impact, Notched Temperature; -30 °C Temperature; 23 °C | 10 kJ/m² 22 kJ/m² |
ISO 179 1eA | ||
Electrical | Nominal Value | Test Method | ||
Volume Resistivity | 1.00e+12 ohms·cm | IEC 60250 | ||
Surface Resistance | 1.00e+13 Ohms | IEC 60250 | ||
Dielectric Constant Frequency; 1000000 Hz Frequency; 100 Hz | 5.00 14.0 |
IEC 60250 | ||
Dissipation Factor Frequency; 1000000 Hz Frequency; 100 Hz | 0.120 0.300 |
IEC 60250 | ||
Comparative Tracking Index | 500 V | IEC 60112 |
Processing | Nominal Value |
Injection | |
Drying Temperature | 80.0 °C |
Drying Time | 4.0 - 8.0 hr |
Rear Temperature | 230 - 250 °C |
Middle Temperature | 230 - 260 °C |
Front Temperature | 230 - 260 °C |
Nozzle Temperature | 250 - 280 °C |
Melt Temperature | 245 - 270 °C |
Mold Temperature | 40 - 80 °C |
Injection Rate | Moderate-Fast |
Back Pressure | 3.00 - 10.0 MPa |
Screw Compression Ratio | 2.5:1.0 |