Product Description | |||
MVR (300°C/1.2 kg) 34 cm³/10 min; light guides; optics and lenses; PC with highest transmission; low viscosity; easy release; injection molding - melt temperature 280 - 320°C | |||
General | |||
Form | Resin Pellets | ||
Feature | Medium-Low Viscosity High Clarity | Easy Release | |
UL Yellow Card | E41613-233174 | ||
Uses Lighting Applications Lenses Optical Applications | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity(23 °C) | 1.19 g/cm³ | ISO 1183 | |
Apparent Bulk Density, Pellets | 0.66 g/cm³ | ISO 60 | |
Melt Volume-Flow Rate, MVR(300 °C;1.2 kg) | 34 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow(2 mm;500 bar;60x60x2mm;280 °C) |
0.70 % | ISO 294-4 | |
Molding Shrinkage, Flow(2 mm;500 bar;60x60x2mm) | 0.65 % | ISO 294-4 | |
Water Absorption, Saturation(23 °C) | 0.30 % | ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) | 0.12 % | ISO 62 | |
Ball Indentation Hardness | 115 MPa | ISO 2039-1 |
Mechanical Nominal Value | Test Method | ||
Tensile Modulus(23 °C) 2350 MPa | ISO 527-2/1 | ||
Tensile Stress, Yield(23 °C) 63.0 MPa | ISO 527-2/50 | ||
Tensile Stress, Break(23 °C) 60.0 MPa | ISO 527-2/50 | ||
Tensile Strain, Yield(23 °C) 6.0 % | ISO 527-2/50 | ||
Tensile Strain, Break(23 °C) 130 % | ISO 527-2/50 | ||
Nominal Tensile Strain at Break(23 °C) > 50 % | ISO 527-2/50 | ||
Flexural Modulus(2 mm/min;23 °C) 2350 MPa | ISO 178 | ||
Flexural Stress 2 mm/min;23 °C 2 mm/min;3.5% Strain;23 °C |
97.0 MPa 73.0 MPa |
ISO 178 | |
Flexural Strain at Flexural Strength(2 mm/min;23 °C) 7.1 % | ISO 178 | ||
C harpy Notched Impact Strength, Complete Break(-30 °C;3 mm) | 12 kJ/m² | ISO 179 1eA | |
C harpy Notched Impact Strength, Partial Break(23 °C;3 mm) | 60 kJ/m² | ISO 179 1eA | |
C harpy Unnotched Impact Strength -60 °C -30 °C 23 °C |
No Break No Break No Break |
ISO 179 1eU | |
Notched Izod Impact Strength, Complete Break(-30 °C;3 12 kJ/m² mm) |
ISO 180/1A | ||
Notched Izod Impact Strength, Partial Break(23 °C;3 mm)55 kJ/m² | ISO 180/1A | ||
Multi-Axial Instrumented Impact Energy -30 °C 23 °C |
60.0 J 55.0 J |
ISO 6603-2 | |
Multi-Axial Instrumented Impact, Peak Force -30 °C 23 °C |
5900 N 4900 N |
ISO 6603-2 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
138 °C 125 °C |
ISO 75-2/B ISO 75-2/A |
Glass Transition Temperature(10 °C;min) | 145 °C | ISO 11357-2 |
Vicat Softening Temperature | 145 °C 146 °C |
ISO 306/B50 ISO 306/B120 |
Ball Pressure Test(136 °C) | Pass | IEC 60695-10-2 |
CLTE, Flow(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse(23 - 55 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
Thermal Conductivity, Across Flow(23 °C) | 0.20 W/m-K | ISO 8302 |
RTI Elec(1.5 mm) | 125 °C | UL 746 |
RTI Imp(1.5 mm) | 115 °C | UL 746 |
RTI Str(1.5 mm) | 125 °C | UL 746 |
Flame Rating, CL 2.9 mm 0.75 mm |
HB V-2 |
UL 94 |
Glow Wire Flammability Index 1 mm 1.5 mm 3 mm |
850 °C 875 °C 930 °C |
IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 0.75 mm 1.5 mm 3 mm |
875 °C 875 °C 900 °C |
IEC 60695-2-13 |
Oxygen Index, Procedure A | 28 % | ISO 4589-2 |
Burning Rate, US-FMVSS( > 1 mm) | passed | ISO 3795 |
Flash Ignition Temperature | 480 °C | ASTM D1929 |
Self Ignition Temperature | 550 °C | ASTM D1929 |
Electrical | Nominal Value | Test Method | |
Surface Resistivity | 1.0E+16 ohms | IEC 60093 | |
Volume Resistivity(23 °C) | 1.0E+16 ohms ·cm | IEC 60093 | |
Electric Strength(23 °C;1 mm) | 34 kV/mm | IEC 60243-1 | |
Relative Permittivity 100 Hz;23 °C 23 °C;1.0e+6 Hz |
3.10 3.00 |
IEC 60250 | |
Dissipation Factor 100 Hz;23 °C 23 °C;1.0e+6 Hz |
5.0E-4 9.5E-3 |
IEC 60250 | |
Comparative Tracking Index, Solution A | 250 V | IEC 60112 | |
Comparative Tracking Index, Solution B | 125 V | IEC 60112 | |
Optical | Nominal Value | Test Method | |
Refractive Index, Method A | 1.584 | ISO 489 | |
Transmittance | 90.0 % 90.0 % > 89.0 % > 89.0 % |
ISO 13468-2 | |
1.0e+3 2.0e+3 3.0e+3 4.0e+3 |
µm µm µm µm |
||
Haze(3.0e+3 µm) | < 0.500 % | ISO 14782 |
Processing | Nominal Value |
Drying Temperature - Dry Air Dryer<Injection> | 120 °C |
Drying Time - Dry Air Dryer<Injection> | 4.0 hr |
Suggested Max Moisture<Injection> | < 0.020 % |
Suggested Shot Size<Injection> | 30 - 70 % |
Rear Temperature<Injection> | 250 - 270 °C |
Middle Temperature<injection> | 270 - 290 °C |
Front Temperature<Injection> | 285 - 305 °C |
Nozzle Temperature<Injection> | 270 - 305 °C |
Processing Temp, Melt<Injection> | 280 - 320 °C |
Mold Temperature<Injection> | 70 - 110 °C |
Back Pressure<Injection> | 10.0 - 20.0 MPa |
Vent Depth <Injection> | 0.025 - 0.075 mm |
Standard Melt Temperature<Injection> | 300 °C |
Hold Pressure<Injection> | 50 - 75 % |
Peripheral Screw Speed <Injection> | 0.05 - 0.2 m/s |