Linear low density polyethylene (LLDPE) is a non-toxic, tasteless and odorless milky white particle with a density of 0.918~0.935g/cm3.It compared with LDPE, have high softening temperature and melt temperature, has good strength and toughness, rigidity, heat resistance, cold resistance is good wait for an advantage, but also has good environmental stress cracking resistance, resistance to impact strength, tear strength and other properties, and acid, alkali, organic solvent and widely used in industry, agriculture, medicine, health and daily life supplies, and other fields.
1, LLDPE film grade
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 2.0±0.4 | g/10min |
| Density | 920±2 | Kg/cm3 |
| Tensile Strengthat Yield | 8 | Mpa ≥ |
| Tensile Strengthat Break | 12 | Mpa ≥ |
| haze | 15 | %≤ |
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 20 | g/10min |
| Density | 0.924 | g/cm3 |
| Tensile Strength | MD12 | Mpa |
| TD 10 | ||
| Elongation at Yield | 13 | % |
| Elongation at Break | 200 | |
| Dark Drop Impact | 105 | g |
| Brittle Temperature(F 50) | -70 | C |
| Vicat Softening Point | 90 | C |
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 3.2 | g/10min |
| Density | 0.939 | g/cm3 |
| Melting Point | 127 | C |
| Tensile Yield Strength | 21 | Mpa |
| Tensile Strength at Break | 28 | Mpa |
| Elongation at Break | 1,100 | % |
| Flexural Modulus | 750 | Mpa |
| Brittle Temperature | <-60 | C |
LLDPE has penetrated almost all traditional markets for polyethylene; it is used for plastic bags and sheets (where it allows using lower thickness than comparable LDPE), plastic wrap, stretch wrap, pouches, toys, covers, lids, pipes, buckets and containers, covering of cables, geomembranes, and mainly flexible tubing.
Company main products:
CONTACT US WITH YOUR NAME, TEL NUMBER, AND EMAIL ADDRESS FOR A QUICK RESPONSE.
WE APPRECIATE SERIOUS INQUIRIES.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}