| Molecular Principal Chain: | Carbon Chain Polymer |
|---|---|
| Color: | Red |
| Appearance: | Red Viscous Liquid |
| Density: | 1.52-1.62 |
| Viscosity: | 9-16 |
| Glass Transition Temperature: | 70-85 |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
| Appearance | Main agent A | Red viscous liquid |
| Curing agent B | Off-white viscous liquid | |
| Density(25ºC) g/cm³ | Main agent A | 1.52-1.62 |
| Curing agent B | 1.72-1.83 | |
| Viscosity (40ºC, mPa.s) | Main agent A | 9-16 |
| Curing agent B | 15-25 |
| Tensile Strength (N/mm2) | 50-70 |
| Elongation at break (%) | 1.8-2.5 |
| Bending Strength (Mpa) | 105-125 |
| Surface Strain (%) | 1.5-1.7 |
| Fracture Ratio (J/m2) | 470-550 |
| Glass Transition Temperature (ºC) | 70-85 |
| Linear Expansion Coefficient(ppm/k, lower than the average of Tg ) | 38-47 |
| Water Absorption(%, 100ºC/24h) | ≤0.5 |
| Thermal Conductivity (W/mK) | 0.8-1.0 |
| Insulation Strength (KV/mm) | 22-28 |
| Dielectric Constant (50Hz) | ≤3.8 |
| Volume Resistivity (Ω/cm) | ≥1.0x1016 |