| Feature: | Plastics |
|---|---|
| CAS No.: | 9003-56-9 |
| Formula: | C45h51n3X2 |
| Samples: |
25kg/bag
|
|---|
| Customization: |
|---|
|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
|---|
| Payment Method: |
|
|---|---|
| Initial Payment Full Payment |
| Currency: | US$ |
|---|
| Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
|---|
Suppliers with verified business licenses
Audited Supplier | General | |||
| Form | Resin Pellets | ||
| Appliances Office supplies Electron & electric parts Automotive |
|||
| Physical | Nominal Value | Test Method | |
| Density / Specific Gravity(23 ºC) | 1.05 g/cm³ | ISO 1183-1 | |
| Melt Flow Rate[MFR] | ISO 1133-1 | ||
| 5 kg;200 ºC | 2.0 g/10min | ||
| 220 ºC;10 kg | 20 g/10min | ||
| Molding Shrinkage(23 ºC) | 0.4 - 0.7 % | ISO 2577 | |
| Hardness, Rockwell R | 108 | ISO 2039-2 | |
| Mechanical | Nominal Value | Test Method | |
| Tensile Strength(50 mm/min) | 47 MPa | ISO 527-2 | |
| Elongation at Break(50 mm/min) | 47 % | ISO 527-2 | |
| Flexural Strength(2 mm/min) | 76 MPa | ISO 178 | |
| Flexural Modulus(2 mm/min) | 2500 MPa | ISO 178 | |
| Notched Izod Impact Strength(23 ºC) | 20 kJ/m² | ISO 180 | |
| Thermal | Nominal Value | Test Method | |
| Deflection Temperature | ISO 75-2 | ||
| 0.45 MPa | 85 ºC | ||
| 1.8 MPa | 77 ºC | ||
| Vicat Softening Point | ISO 306 | ||
| 1 kg;120 ºC/h | 102 ºC | ||
| 5 kg;50 ºC/h | 95 ºC | ||
| Flammability | UL 94 | ||
| 1.6 mm | HB | ||
| 0.8 mm | HB | ||
| Electrical | Nominal Value | Test Method | |
| Specific volume resistivity | 1.0E+14 ohms· m | IEC 60093 | |
| Dielectric Strength | 22 kV/mm | IEC 60243-1 | |
| Product Description | ||||
| A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation. | ||||
| General | ||||
| Form | Resin | Pellets | ||
| Physical | Nominal Value | Test Method | ||
| Density / Specific Gravity | 1.40 g/cm³ | |||
| Water Absorption | 0.21 % | ASTM D570 | ||
| Moisture Absorption at Equilibrium | 0.80 % | ASTM D570 | ||
| Linear Mold Shrinkage | 2.2 % | |||
| Linear Mold Shrinkage, Transverse | 1.8 % | |||
| Hardness, Rockwell R | 111 | ASTM D785 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Strength, Yield | 37.0 MPa | ASTM D638 | ||
| Elongation at Break | 30 % | ASTM D638 | ||
| Flexural Strength | 52.0 MPa | ASTM D790 | ||
| Flexural Modulus | 2100 MPa | ASTM D790 | ||
| Compressive Strength | 66.0 MPa | ASTM D695 | ||
| Shear Strength | 40.0 MPa | ASTM D732 | ||
| Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C |
50 J/m 30 J/m |
ASTM D256 | ||
| Thermal | Nominal Value | Test Method | ||
| Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
152 °C 106 °C |
ASTM D648 | ||
| Flammability, UL94 | HB | UL 94 | ||