| Type: | CFC |
|---|---|
| Composition: | Carbon Fiber |
| Carbon Content: | High-Carbon |
| Grade: | Industrial Grade |
| Forming Way: | Hot Press |
| Crystal Morphology: | Compact Crystalline Graphite |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
| Material | CFC laminates |
| Grade | FTCY-CFC |
| Bulk Density(g/cm3) | 1.4~1.5 |
| Carbon Content(%) | ≥98.5-99.9 |
| Bending Strength(MPa) | 100~150 |
| Tensile Strength(MPa) | 90~130 |
| Flexural Strenth(MPa) | 100-200 |
| Interlaminar Shear Strength(MPa) | ≥13 |
| Compressive Strength(MPa) | 130~170 |
| Tensile modulus(GPa) | 25~35 |
| Coefficient of Linear Expansion(10-6/K) | 0.3~1.2 |
| Resistivity(μΩ·k) | 30~43 |
| Thermal Conductivity(W/m·k) | 10-30 |
| Ash(PPM) | ≤65 |
| Processing Temperature(ºC) | 2400 |
| Material | CFC woven |
| Grade | FTZC-C/C |
| Bulk Density(g/cm3) | 1.5~1.8 |
| Bending Strength(MPa) | 120~180 |
| Tensile Strength(MPa) | 100~140 |
| Interlaminar Shear Strength(MPa) | 10~15 |
| Z-direction Compressive Strength(MPa) | 120~150 |
| XY -direction Compressive Strength(MPa) | 180~250 |
| Tensile Modulus(GPa) | 25~35 |
| Coefficient of Linear Expansion(10-6/K) | 0.5~1.3 |
| Resistivity(μΩ·k) | 15~40 |
| Thermal Conductivity(W/m·k) | 30-50 |
| Ash(PPM) | ≤100 |