Feature: | Plastics |
---|---|
CAS No.: | 9003-56-9 |
Formula: | C45h51n3X2 |
Samples: |
25kg/bag
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||
Features: High flow; good paint finish; easy to make large molded parts Application: Paintable two-wheeler applications | |||
General | |||
Form | Resin Pellets | ||
Feature Good Adhesion Excellent Processability | |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity(23 °C) | 1.04 g/cm³ | ISO 1183 | |
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 50 cm³/10 min | ISO 1133 | |
Molding Shrinkage | 0.40 - 0.70 % | ISO 294-4 | |
Mechanical | Nominal Value | Test Method | |
Tensile Stress, Yield(50 mm/min) | 41.0 MPa | ISO 527-2/50 | |
Tensile Stress, Break(50 mm/min) | 30.0 MPa | ISO 527-2/50 | |
Tensile Strain, Break(50 mm/min) | 70 % | ISO 527-2/50 | |
Flexural Modulus(2 mm/min) | 2100 MPa | ISO 178 | |
Flexural Stress(2 mm/min) | 61.0 MPa | ISO 178 | |
Charpy Notched Impact Strength(23 °C) | 20 kJ/m² | ISO 179 | |
Notched Izod Impact Strength(23 °C) | 19 kJ/m² | ISO 180/1A | |
Thermal | Nominal Value | Test Method | |
Deflection Temperature Under Load, Annealed(1.8 | MPa) 96.0 °C | ISO 75-2/A | |
Vicat Softening Temperature 5 kg;50 ºC/hr 50 ºC/hr;1 kg |
99.0 °C 104 °C |
ISO 306/B50 ISO 306/A50 |
|
CLTE, Flow | 8.3E-5 cm/cm/°C | ISO 11359-2 | |
Flame Rating(1.5 mm) | HB | UL 94 | |
Processing | Nominal Value | ||
Drying Temperature | 80 - 85 °C | ||
Drying Time | 2 - 4 °C | ||
Barrell Temperature - Front | 190 - 230 °C | ||
Barrell Temperature - Middle | 190 - 230 °C | ||
Barrell Temperature - Rear | 180 - 220 °C | ||
Mold Temperature | 30 - 60 °C |