Name: | Polypropylene PP Raffia |
---|---|
Process: | Extrusion |
Application: | Weaving Ribbons Bags |
Samples: |
customize according to your exact requirements
|
---|
Customization: |
---|
Shipping Cost:
Estimated freight per unit. |
about shipping cost and estimated delivery time. |
---|
Payment Method: | |
---|---|
Initial Payment Full Payment |
Currency: | US$ |
---|
Return&refunds: | You can apply for a refund up to 30 days after receipt of the products. |
---|
Suppliers with verified business licenses
Product Description | |||||
Polypropylene copolymer, flame retardant grade UL94 V-2, halogen free, antymony oxidefree | |||||
General | |||||
Form Resin Pellets | |||||
Feature |
Non-Brominated & Non- Chlorinated Flame Retardant |
Antimony Free | Ec 1907/2006 (Reach) | ||
UL Yellow Card | E477602-102433017 | ||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 0.990 g/cm³ | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 10 g/10min | ASTM D1238 | |||
Molding Shrinkage | 1.2 % | Internal Method | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Yield | 25.0 MPa | ASTM D638 | |||
Tensile Elongation, Break | 40 % | ASTM D638 | |||
Flexural Modulus | 1700 MPa | ASTM D790 | |||
Notched Izod Impact 0 °C 23 °C |
25 J/m 40 J/m |
ASTM D256 | |||
Thermal | Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 55.0 °C | ASTM D648 | |||
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 75.0 °C | ASTM D1525 | |||
Ball Pressure Test(125 °C) | Pass | IEC 335 | |||
Flame Rating 1.6 mm 3.2 mm |
V-2 V-2 |
UL 94 | |||
Glow Wire Ignition Temperature [GWIT] | 960 °C | IEC 60695-2-13 | |||
Oxygen Index | 26 % | ASTM D2863 | |||
Needle Flame Test | Pass | IEC 60695-11-5 | |||
Electrical | Nominal Value | Test Method | |||
Comparative Tracking Index | 600 V | IEC 60112 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 60 °C | ||||
Drying Time<Injection> | 2.0 hr | ||||
Rear Temperature<Injection> | 180 °C | ||||
Middle Temperature<injection> | 190 °C | ||||
Front Temperature<Injection> | 200 °C | ||||
Mold Temperature<Injection> | 20 - 40 °C |
0.9 g/cm³
ASTM D1505
3 g/10min
1 °C
1 kg
ISO 1133
1550 MPa
ISO 527-2/1A
37.0 MPa
10 %
ISO 527-2/1A
4.5 kJ/m²
1 °C
ISO 179 1eA
3.5 kJ/m²
1 °C
ISO 180/1A
85.0 °C
1 MPa
ISO 75-2/B
55.0 °C
1 MPa
ISO 75-2/A
150 °C
ISO 306/A120
85.0 °C
ISO 306/B120