| Material: | Polyvinyl Chloride/PVC |
|---|---|
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Extrusion |
| Color: | Any Colors Can Be Customized |
| Appreance: | Granules Compounds Particles |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Product Description: |
| Characteristics and Application |
| Processing Indicator |
| Machine Barrel Temperature | Molding Temperature |
| 145-165ºC | 165-175ºC |
| Physical and Electrical Properties |
| No | Item | Unit | RY-H7031VC | RY-H7032VC | RY-H7033VC | RY-H7034VC |
| 1 | Tensile Strength | MPa | ≥15 | ≥15 | ≥15 | ≥15 |
| 2 | Elongation at Break | % | ≥180 | ≥180 | ≥180 | ≥180 |
| 3 | Thermal Deformation | % | ≤50 | ≤50 | ≤50 | ≤50 |
| 4 | Thermal stability time at 200ºC | min | ≥50 | ≥50 | ≥50 | ≥50 |
| 5 | Volume Resistivity at 20ºC | Ω.m | ≥1.0×108 | ≥1.0×108 | ≥1.0×108 | ≥1.0×108 |
| 6 | Dielectric Strength | MV/m | ≥18 | ≥18 | ≥18 | ≥18 |
| 7 | Brittle Temperature with Impact | ºC | -25 | -30 | -35 | -40 |
| 9 | Thermal Aging Performance | ºC*h | 100±2ºC×168h | |||
| Tensile Strength After Aging | MPa | ≥15 | ≥15 | ≥15 | ≥15 | |
| Tensile Strength Variation | % | ±20 | ±20 | ±20 | ||
| Elongation After Aging | % | ≥180 | ≥180 | ≥180 | ≥180 | |
| Elongation Variation | % | ±20 | ±20 | ±20 | ±20 | |
| Mass Loss | g/m2 | ≤23 | ≤23 | ≤23 | ≤23 | |
| Package, Transportation and Storage |