After-sales Service: | Available |
---|---|
Warranty: | 10 Years |
Type: | Steel Coil |
Standard: | ASTM, AISI, GB, JIS, DIN, BS |
Certification: | ISO, CE |
Surface Treatment: | Tin Plating / Color Coating |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Available Sizes | |||
Item | Coil | Sheet | Tolerance |
Annealing | BA/ CA | BA/ CA | - |
Thickness | 0.14 - 0.55 mm | 0.14 - 0.55 mm | ± 3% |
Width | 700 - 1,050 mm | 700 - 1,050 mm | -0/ +2mm |
Length | - | 500 - 1,200 mm | -0/ +2mm |
Weight | 3 - 15 MT per coil | 2 MT Max per bundle | ± 0.3% |
Inside Diameter | 420/ 508 mm | - | ± 10mm |
Outside Diameter | 1,800 mm | - | - |
Remark | Temper | Hardness (HR30T) |
Yield Strength (Mpa) |
Features | Typical Application | ||
JIS G3303-2008 |
ASTM A623M-06a |
DIN EN10202-2001 |
|||||
Single Reduced (SR) |
T-1 | T49 | TS230 | 49 ± 3 | 230 ±50 | Deep drawing which requires large flexibility. | Drawn and ironed cans, nozzles, spouts, closures, mounting cup, oil filter. |
T-2 | T53 | TS245 | 53 ± 3 | 245 ±50 | Moderate drawing with some stiffness. | Ring and plugs, dome tops, closures, shallow drawn parts. Drawing can, body, end for large can. | |
T-2.5 | T54 | TS260 | 55 ± 3 | 260 ±50 | Combines the drawability of T-2 and the stiffness of T-3. | Battery shells, small can ends and bodies | |
T-3 | T57 | TS275 | 57 ± 3 | 275 ±50 | Shallow drawing, proper stiffness to minimize fluting and prevent buckling. | Top and bottom of cans, can ends and bodies, large diameter closures, crown caps. | |
T-3.5 | T59 | TS290 | 59 ± 3 | 290 ±50 | Items that require better formability than T-4. | General use, pail, 18L, 4L | |
T-4 | T61 | TH415 | 61 ± 3 | 415 ±50 | Moederate forming. Moderate (comparatively large) stiffness. |
Can bodies and ends, crown caps, closures. Body and end for small can. |
|
T-5 | T65 | TH435 | 65 ± 3 | 435 ±50 | High Stifness, excellent buckling resistance. Increased stiffness to resist buckling. | Can ends and bodies requiring intensity. Body and end for small can. |
|
Double Reduced (DR) |
DR-7M | T71 | TH520 | 71 ± 5 | 520 ±50 | Moderate strength and stiffness with moderate forming. | DRD bodies, dome, Lug cap & 3 piece bodies |
DR-8 | T72 | TH550 | 73 ± 5 | 550 ±50 | High strength and stiffness. | DRD bodies, end, Lug cap & 3 piece bodies | |
DR-8M | T73 | TH580 | 73 ± 5 | 580 ±50 | |||
DR-9 | T75 | TH620 | 76 ± 5 | 620 ±50 | Higher strength and stiffness. | DRD bodies, Lug cap & 3 piece bodies Thnner guage body, end, DRD cans, caps. |
|
DR-9M | T76 | - | 77 ± 5 | 660 ±50 | |||
DR-10 | - | - | 80 ± 5 | 690 ±50 | Very large stiffness and strength | DRD bodies, Lug cap & 3 piece bodies Thnner guage body, end, DRD cans, caps. |
|
Note: Making cans with DR materials, please pay a special attention to the rolling direction. |
1. Type of Steel | |
MR | It contains few residual minor constituents and has good corrosion resistance. |
It is widely used for the applications of containers. | |
L | It contains particularly few residual minor constituents as Cu, Ni, Cr, Mn. |
It is suitable for the materials of containers requiring improved corrosion resistance. | |
D | It is an aluminum killed steel. It is suitable for the applications. |
that bear deep drawing or other workings which may produce Luder's lines patterns. |
2. Surface finish | ||||||
Product Finish |
Code | Steel base | Product | Flow-melted | Nominal surface roughness of the steel base | |
Euro | China | Ra (μm) | ||||
Bright | BR | B | smooth | Tinplate | Yes | ≤ 0.35 |
Fine stone | FS | R | fine stone | Tinplate | Yes | 0.25 - 0.45 |
Stone | ST | R2 | stone | Tinplate | Yes | 0.35 - 0.60 |
Silver | SG | S | shot blast | Tinplate | Yes | ≥ 0.90 |
Matt | MM | M | shot blast | Tinplate | No | Various |
Fine stone | FS | R2 | fine stone | TFS/ ECCS | - | 0.25 - 0.45 |
Stone | ST | R1 | stone | TFS/ ECCS | - | 0.35 - 0.60 |
Note 1 | Double reduced product is only supplied as stone finish | |||||
Note 2 | Sub-classfied based on the surface finishing of the blackplate. | |||||
Note 3 | The appearance is governed by: | |||||
a) | the surface characteristics of the steel base which principally result from controlled preparation of the work rolls used during the final stages of temper rolling; | |||||
b) | the mass of the coating applied; and | |||||
c) | whether the tin layer is flow-melted or unflow-melted. | |||||
Surface finish | Characteristic | |||||
Bright finish | Glazed surface obtained after melting treatment of electrotinned smooth raw materail strip with extremely fine rubstone fingure by processing. | |||||
Stone finish | Glazed surface obtained after melting treatment of electrotinned smooth raw materail stripfeaturing certain rubstone figures. | |||||
Silver finish | Glazed surface obtained after melting treatment of electrotinned smooth raw material strip with rough matt furface. | |||||
Matte finish | Matt surface of general matt raw material strip without melting treatment. |
3. Coating Weight | ||||
1) Tinplate (ETP) | ||||
Former Coating | Coating Weight | Nominal Coating Weight | Minimum average | |
Designation | Code | (g/m2) | (g/m2) | |
Equally Coated |
10# | 1.1/ 1.1 | 1.1/ 1.1 | 0.9/ 0.9 |
20# | 2.2/ 2.2 | 2.2/ 2.2 | 1.8/ 1.8 | |
25# | 2.8/ 2.8 | 2.8/ 2.8 | 2.5/ 2.5 | |
50# | 5.6/ 5.6 | 5.6/ 5.6 | 5.2/ 5.2 | |
75# | 8.4/ 8.4 | 8.4/ 8.4 | 7.8/ 7.8 | |
100# | 11.2/ 11.2 | 11.2/ 11.2 | 10.1/ 10.1 | |
Differentially Coated |
25#/ 10# | 2.8/ 1.1 | 2.8/ 1.1 | 2.5/ 0.9 |
50#/ 10# | 5.6/ 1.1 | 5.6/ 1.1 | 5.2/ 0.9 | |
50#/ 25# | 5.6/ 2.8 | 5.6/ 2.8 | 5.2/ 2.5 | |
75#/ 25# | 8.4/ 2.8 | 8.4/ 2.8 | 7.8/ 2.5 | |
75#/ 50# | 8.4/ 5.6 | 8.4/ 5.6 | 7.8/ 5.2 | |
100#/ 25# | 11.2/ 2.8 | 11.2/ 2.8 | 10.1/ 2.5 | |
100#/ 50# | 11.2/ 5.6 | 11.2/ 5.6 | 10.1/ 5.2 | |
100#/ 75# | 11.2/ 8.4 | 11.2/ 8.4 | 10.1/ 7.8 | |
125#/ 50# | 15.1/ 5.6 | 15.1/ 5.6 | 13.9/ 5.2 | |
Differential Marking | ||||
a) Edge Marking : Low Coating Side with interrupted lines | ||||
b) Line Marking : Heavy Coating Side with continuous lines | ||||
c) Tin coating weight can be flexibly adjusted according to customer's requirement |
4. Passivation | ||
Item | Chromium weight - Min | Chromium weight - Max |
(mg/m2) - Each Side | (mg/m2) - Each Side | |
Code 311 | 3.5 | 9.0 |
Code 300 | 1.0 | 3.0 |
Notes | 1) Passivation applys to Tinplate only. | |
2) Code 311 is the most widely used passivation. | ||
3) Code 300 is a simple chemical dip treatment. |
5. Oiling | ||
Item | Oil Weight | Aim Oil Weight |
(mg/m2) - Each Side | (mg/m2) - Each Side | |
Slightly | 1.0 - 3.5 | 2.5 |
Normal | 3.0 - 6.0 | 4.5 |
Medium | 6.0 - 9.0 | 7.5 |
Light Heavy | 7.0 - 11.0 | 8.5 |
Heavy | 10.0 Min | 9.5 |
Remarks: | Tinplate and TFS are electro statically oiled with DOS (Di-Octyl-Sebacate). |
Package
|
Standard export seaworthy package,suit for all kinds of transport, or as required.
|
Water-proof Paper + Edge protection + Wooden Pallets
|
|
Bulk Size
|
Any size
|
Loading Port
|
Tianjin, Qingdao Port or any China Seaport
|
Container
|
1*20ft container load Max. 25 Ton, Max. length 5.8m
|
1*40ft container load Max. 25 Ton, Max. Length 11.8m
|
|
Delivery Time
|
7-15 days or according to the order's quantity
|
Q1:What are your company's main products ?
A1: Our main products are stainless steel/carbon/galvanized plate/sheet, coil, round/square pipe, bar, channel, etc.
Q2. How do you control quality ?
A2: Mill Test Certification is supplied with shipment, Third Party Inspection is available.
Q3. What are the advantages of your company ?
A3: We have many professionals, technical personnel, more competitive prices and best after-dales service than other steel companies
Q4. How many coutries you already exported ?
A4: Exported to more than 50 countries mainly from America, Russia, UK, Kuwait, Egypt, Turkey, Jordan,India, etc.
Q5. Can you provide sample ?
A5: Small samples in store and can provide the samples for free.
Customized samples will take about 5-7days.
Suppliers with verified business licenses