| Feature: | Hydrolytic Degradable |
|---|---|
| Material: | Polyethylene/PE |
| Usage: | General Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Extrusion |
| Color: | White |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier | Product Description and Application |
| Application: |
| Technical Properities: |
| Item | Unit | RY-XL10 | RY-XL35 | RY-XL66 | RY-XL110 | RY-XL220 |
| Tensile Strength | ≥Mpa | 13.5 | 13.5 | 17 | 17 | 17 |
| Elogation at break | % | 350 | 350 | 500 | 500 | 500 |
| (Oven Aging 135ºC*168h) | ||||||
| Change rate of Tensile Strength | ≤% | ±20 | ±20 | ±20 | ±20 | ±20 |
| Change rate of Elogation at break | ≤% | ±20 | ±20 | ±20 | ±20 | ±20 |
| (Hot Set Test) 200ºC*0.2MPa*15min | ||||||
| Hot Elogation | ≤% | 80 | 80 | 80 | 80 | 80 |
| Permanent deformation rate | ≤% | 5 | 5 | 5 | 5 | 5 |
| Dissipation Factor | ≤ | 5×10-4 | 5×10-4 | 3×10-4 | 3×10-4 | 3×10-4 |
| Dielectric Constant | ≤ | 2.35 | 2.35 | 2.35 | 2.35 | 2.35 |
| DC Volume Resistivity | ≥Ω ·m | 1×1014 | 1×1014 | 1×1014 | 1×1014 | 1×1014 |
| Dielectric Strength | ≥ MV/m | 25 | 25 | 35 | 35 | 40 |
| Degree of Crosslinking | ≥% | 80 | 80 | 82 | 82 | 82 |
| Applications | Crosslinkable polyethylene insulation material for wires and cables up to 10kV |
Crosslinkable polyethylene insulation material for wires and cables up to 35kV |
Crosslinkable polyethylene insulation material for wires and cables up to 66kV |
Crosslinkable polyethylene insulation material for wires and cables up to 110kV |
Crosslinkable polyethylene insulation material for wires and cables up to 220kV |
|
| Package, Transportation and Storage |
| Company Profile |
| Workshop |
| Test Equipments |
| Certificate& Test reports |
| FAQ |
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}