| CAS No.: | 63231-66-3 |
|---|---|
| Formula: | [CH2-Chcl-CH2-CH2]N |
| EINECS: | No |
| Appearance: | Powder |
| Usage: | Rubber Auxiliary Agents, Plastic Auxiliary Agents |
| Color: | White |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Chemical Raw Material CPE 135A Chlorinated Polyethylene (CPE 135) and PVC Raw Material
Chrinated Polyethylene Resin CPE Description
SHENGXING Chlorinated Polyethylene Resin (CPE) is an excellent impact modifier, which is widely used in PVC pipes, pipe fittings, profiles, plates and other hard plastic products. With excellent weather resistance, ozone resistance, chemical resistance and aging resistance, and good oil resistance, flame retardant and coloration performance, it can greatly improve the impact strength of products. It is a kind of plastic modified material with good performance.
CPE can be used in plastic products and rubber products, we can design and produce different CPE according to customers' requirements, OEM and ODM is acceptable.
Chlorinated Polyethylene Resin CPE Photos
Chlotinated Polyethylene Resin CPE Technical Data
Technical Data Sheet I
| Item | CPE 8100 | CPE 135A | CPE 135AL | CPE 3510 |
| Chlorine Content % | 30±1 | 36±1 | 36±1 | 36±1 |
| Heat of fustion J/g≤ | 1.5 | 2 | 2 | 2 |
| Volatile Matter %≤ | 0.3 | 0.3 | 0.3 | 0.3 |
| Impurity Particles pcs/200g≤ | 40 | 40 | 40 | 40 |
| Shore A Hardness ≤ | 65 | 60 | 60 | 60 |
| Tensile Strength MPa≥ | 8 | 8 | 8 | 8 |
| Elongation at Break %≥ | 700 | 700 | 700 | 1000 |
| Application | Replace MBS as impact modifier for translucent PVC products | Impact modifier in high speed extrusion PVC products | Impact modifier in PVC products | Impact modifier in PVC products |
| Property | Good processability and impact resistance. | Promote the rapid plasticization of PVC, good impact resistance | High impact resistance, high filling property | Rapid plasticization, high impact modification performance, high filling property |
| Item | CM3550 | CM 3565 | CM 3575 | CM 3580 |
| Chlorine Content % | 35±1 | 35±1 | 35±1 | 35±1 |
| Volatile Matter %≤ | 0.3 | 0.3 | 0.3 | 0.3 |
| Impurity Particles pcs/200g≤ | 40 | 40 | 40 | 40 |
| Shore A Hardness ≤ | 55 | 55 | 55 | 60 |
| Tensile Strength MPa≥ | 8 | 8 | 8 | 8 |
| Elongation at Break %≥ | 700 | 700 | 700 | 700 |
| Mooney Viscosity ML(1+4) 125 ºC | 50±5 | 65±5 | 75±5 | 80±5 |
| Application | Rubber hoses, foaming products, wires or cables | Cables or wires, many rubber products | Cables, wires, rubber hoses and other rubber products | Cables and wires, rubber hoses and other rubber products |
| Properties | Low mooney viscosity, good processing performance | Relatively low mooney viscosity, excellent processing performance. | High tensile strength, good filling performance | High tensile strength, excellent processing performance. |