Description: NV 7030 is a blend of nitrile rubber and PVC. After adding vulcanizing agent, the compound is vulcanized and formed (the vulcanizing agent is selected according to the process requirements).
Special properties:
Calendering and pressing out are fast and the surface is smooth
Good storage stability
Excellent abrasion & tear resistance
Ozone resistance & excellent weather resistance
Excellent oil and solvent resistance
Excellent antistatic property
Excellent flame retardancy
Characteristics:
Type (according to GB/T 5576-1997)NBR+PVC............NBR+PVC
B-AN.......................................34%
ML 1+4@100ºC ..............................…60±10
Volatile matter................................. under 1.0%
Natural color.................................…Black
Properties after working:
Sulfur (covered with 2% magnesium carbonate) and overspeed thiuram accelerator TMTD and subsulfonamide retarder CZ are added at 170 ºC × Vulcanization under 6min.
Standard formula:
NV 7030 |
100 |
SRF,N774 |
60 |
DOP |
20 |
ZNO |
5 |
RD |
1.0 |
SA |
1.0 |
2%MgO3 Coated,Sulfur |
0.5 |
CZ |
1.5 |
TMTD(TT) |
1 |
Mechanical properties: NBR + PVC compound and vulcanizate
Item |
Test method |
Unit |
Measured value |
Final value |
Mooney viscosity(ML 1+4@100ºC) |
52 |
Rheometer properties:ODR Rheometer170ºC×12min×1arc |
Minimum torque |
/ |
lb-in |
2.84 |
2.84 |
Maximum torque |
/ |
lb-in |
23.07 |
23.07 |
Scorch time TS1 |
/ |
min |
1.6 |
1.6 |
Optimum cure TC90 |
/ |
min |
5.8 |
5.8 |
1,Mechanical properties 1.1 Cured 170ºC×6min |
Proportion |
ASTM D297 |
g/cm3 |
1.172 |
1.172 |
Hardness |
ASTM D2240 |
Points |
79 |
80 |
80 |
80 |
Tensile Strength |
ASTM D412 |
Kg/cm2 |
159 |
162 |
165 |
162 |
Elongation |
% |
478 |
472 |
470 |
472 |
M200 |
Kg/cm2 |
101 |
102 |
106 |
102 |
1,Mechanical properties 1.2 Heat resistant air aging at 100ºC×70hrs |
Hardness Change |
ASTM D2240 |
Points |
-4 |
-5 |
-6 |
-5 |
Tensile Change |
ASTM D412 |
% |
+0.28 |
+0.30 |
+0.31 |
+0.30 |
Elongation Change |
ASTM D412 |
% |
-17 |
-16.8 |
-17.5 |
-17 |
2,Oil resistance 2.1 ASTM NO.1 Oil Immersion at 100ºC×70h |
Hardness Change |
ASTM D2240 |
Points |
+5 |
+6 |
+6 |
+6 |
Tensile Change |
ASTM D412 |
% |
-0.93 |
-0.98 |
-0.98 |
-0.93 |
Elongation Change |
ASTM D412 |
% |
-26 |
-27 |
-27 |
-27 |
Volume Change |
ASTM D471 |
% |
-6.70 |
-6.87 |
-6.87 |
-6.87 |
2,Oil resistance 2.2 ASTM NO.903 Oil Immersion at 100ºC×70hrs |
Hardness change |
ASTM D2240 |
Points |
+4 |
+4 |
+5 |
+4 |
Tensile Change |
ASTM D412 |
% |
+1.85 |
+1.84 |
+1.85 |
+1.85 |
Elongation Change |
ASTM D412 |
% |
-15.1 |
-15 |
-15.2 |
-15 |
Volume Change |
ASTM D471 |
% |
+0.21 |
+0.20 |
+0.20 |
+0.20 |
2,Oil resistance 2.3 Fuel C Immersion at 40ºC×48hrs |
Volume Change |
ASTM D471 |
% |
+30.66 |
+30.65 |
+30.67 |
+30.66 |
3,Compression set at 100ºC×70hrs(The vulcanization condition of the sample used in the experiment is 170 ºC×10min) |
Deformation Rate |
ASTM D395 |
% |
46.10 |
46.00 |
45.98 |
46.00 |
4,Static ozone resistance at 80pphm×20%elongation×40ºC×120hrs |
Crack or No crack |
ASTM D1171 |
/ |
No |
No |
No |
No |
Packaging:25 kg per cardboard boxes.
Storage and shelf life:
NV 7030 may be stored in its original unopened packaging at a temperature below 40°C for up to 18 months as from the date of manufacture marked clearly on the packaging.
Q: Are you a factory or trading company?
A: We are rubber raw material manufacturer and owned 3 factories.
Q: Where is the loading port and How do you ship the goods?
A: Our factory is nearby Shanghai Port, but loading port can be negotiated. We could ship by sea, by air or by express(EMS, UPS, DHL, TNT, FEDEX and etc). Please confirm with us before placing orders.
Q: How can we guarantee the products' quality?
A: All the products must be tested refers to key specifications during the production and final inspection before shipment.
Q: What about the lead time?
A: It depends on the order quantity you place the order. Usually sample needs 5-8 working days, mass production needs 15-30 days.