| Carbon Content: | High-Carbon |
|---|---|
| Grade: | Industrial Grade |
| Forming Way: | Isostatic Graphite |
| Density: | 1.72 to 1.85 g/cm3 |
| Specific Resistance: | No More Than 8.5 |
| Compressive Strenght: | 34 MPa Min |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Property (Typical Value) |
TSK | GSK | Unit |
| Apparent Density | ≥1.68 | ≥1.72 | g/cm3 |
| Max Grain Size | ≤2 | ≤0.8 | mm |
| Specific Electrical Resistivity | 8-10 | ≤8.5 | μΩm |
| Flexural Strength | ≥12.5 | ≥15 | Mpa |
| Compressive Strength | ≥28 | ≥35 | Mpa |
| Porosity | ≤24 | ≤20 | % |
| Ash value | ≤0.3 | ≤0.3 | % |
| Property (Typical Value) |
HTG-4 | HTG-5 | Unit |
| Apparent Density | ≥1.78 | ≥1.85 | g/cm3 |
| Max Grain Size | ≤43 | ≤43 | µm |
| Ash value | ≤500 | ≤500 | ppm |
| Specific Electrical Resistivity | ≤12 | ≤10 | μΩm |
| Flexural Strength | ≥35 | ≥40 | Mpa |
| Compressive Strength | ≥60 | ≥70 | Mpa |
| Shore Hardness | ≥40 | ≥45 | HSD |
| Thermal Expansion (room temperature to 600ºC) | ≤4.5 | ≤4.4 | 10-6/ºC |
| Property (Typical Value) |
HTD-5 | HTD-6 | HTD-7 | HTD-8 | HTD-9 | Unit |
| Apparent Density | 1.85 | 1.90 | 1.82 | 1.90 | 1.82 | g/cm3 |
| Max Grain Size | 13-15 | 8-10 | 8-10 | 8-10 | µm | |
| Ash Content | ≤500 | ≤500 | ≤500 | ≤500 | ≤500 | ppm |
| Purified ASH Content | 50 | 50 | 50 | 50 | 50 | ppm |
| Specific Electrical Resistivity | 8-10 | 8-9 | 11-13 | 11-13 | 11-13 | μΩm |
| Flexural Strength | 46 | 55 | 51 | 60 | 59 | Mpa |
| Compressive Strength | 85 | 95 | 115 | 135 | 121 | Mpa |
| Shore Hardness | 48 | 53 | 65 | 70 | 70 | HSD |
| Thermal Expansion (room temperature to 600ºC) | 4.75 | 4.8 | 5.8 | 5.85 | 5.85 | 10-6/ºC |