ABS FOR Light resistance; Heat resistance High impact resistance Fax machines projectors
https://forever-plastics.en.made-in-china.com/product-list-1.html
Product Description | |||||
Features: Light resistance; Heat resistance; High impact resistance; 1.5mm V-0; 2.5mm 5VA Applications: Displays; Chassis; Modems; Power Panels; Power Outlets; Car Batteries; Fax machines; projectors; large all-in-ones; coffee machines; TV front and rear frames and car audio consoles Weather Resistant | |||||
General | |||||
Form | Resin Pellets | ||||
Feature | Outdoor | Good Thermal | High Impact | ||
UL Yellow Card E56070-508235 |
|||||
Uses Light Covers | Printer Parts | Panel |
|||
Socket | Printer Chassis | Remote Controls | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity(23 °C) | 1.19 g/cm³ | ISO 1183 | |||
Melt Volume-Flow Rate, MVR(220 °C;10 kg) | 25 cm³/10 min | ISO 1133 | |||
Molding Shrinkage | 0.30 - 0.60 % | ISO 294-4 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Yield(50 mm/min) | 38.0 MPa | ISO 527-2/50 | |||
Tensile Strength, Break(50 mm/min) | 29.0 MPa | ISO 527-2/50 | |||
Tensile Elongation, Break(50 mm/min) | 15 % | ISO 527-2/50 | |||
Flexural Modulus(2 mm/min) | 2000 MPa | ISO 178 | |||
Flexural Strength(2 mm/min) | 58.0 MPa | ISO 178 | |||
C harpy Notched Impact Strength -30 °C 23 °C |
12 kJ/m² 23 kJ/m² |
ISO 179 | |||
Notched Izod Impact -30 °C 23 °C |
11 kJ/m² 22 kJ/m² |
ISO 180/1A | |||
Thermal Nominal Value | Test Method | ||||
Deflection Temperature Under Load, Unannealed(1.8 MPa) | 86.0 °C | ISO 75-2/A | |||
Deflection Temperature Under Load, Annealed(1.8 MPa) | 96.0 °C | ISO 75-2/A | |||
Vicat Softening Temperature | |||||
5 kg;50 ºC/hr | 96.0 °C | ISO 306/B50 | |||
50 ºC/hr;1 kg | 103 °C | ISO 306/A50 | |||
CLTE, Flow | 8.5E-5 cm/cm/°C | ISO 11359-2 | |||
Flame Rating 1.5 mm 2.5 mm |
V-0 5VA |
UL 94 | |||
Processing | Nominal Value | ||||
Drying Temperature<Injection> | 80 - 85 °C | ||||
Drying Time<Injection> | 2.0 - 4.0 hr | ||||
Rear Temperature<Injection> | 180 - 210 °C | ||||
Middle Temperature<injection> | 190 - 220 °C | ||||
Front Temperature<Injection> | 190 - 220 °C | ||||
Mold Temperature<Injection> | 40 - 70 °C | ||||
Injection Pressure<Injection> | 4.90 - 7.85 MPa | ||||
Holding Pressure<Injection> | 1.96 - 4.90 MPa | ||||
Back Pressure<Injection> | 0.490 - 0.981 MPa |