Product Description
LNP FARADEX AS002 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% stainless steel fiber. Added features of this grade include: Electrically Conductive, EMI/RFI shielding.
General
Form	Resin Pellets
Filler 10 % Stainless Steel Fiber
Feature Electrically Conductive Emi/Rfi Shielding
Consumer Electrical		Packaging	Industria
Physical		Nominal Value	Test Method
Density / Specific Gravity		1.12 g/cm³ 1.11 g/cm³	ASTM D792 ISO 1183
Moisture Absorption(23 °C;50% RH/24 hrs)		0.2 %	ASTM D570
Mold Shrinkage, Flow 24 hrs 24 hrs		0.18 % 0.18 %	ASTM D955 ISO 294
Mold Shrinkage, XFlow 24 hrs 24 hrs		0.27 % 0.27 %	ASTM D955 ISO 294

Mechanical	Nominal Value	Test Method
Izod Impact, Unnotched 23 °C 80104;23 °C	286 J/m 20 kJ/m²	ASTM D4812 ISO 180/1U
Izod Impact, Notched 23 °C 80104;23 °C	58 J/m 7 kJ/m²	ASTM D256 ISO 180/1A
Instrumented Dart Impact, Energy at Peak(23 °C)	11 J	ASTM D3763
Tensile Stress, Yield	42 MPa	ASTM D638
Tensile Stress, Yield	39 MPa	ISO 527
Tensile Stress, Break	39 MPa	ASTM D638
Tensile Stress, Break	37 MPa	ISO 527
Tensile Strain, Yield	2.2 %	ASTM D638
Tensile Strain, Yield	2.2 %	ISO 527
Tensile Strain, Break	8.6 %	ASTM D638
Tensile Strain, Break	3.3 %	ISO 527
Tensile Modulus 50 mm/min 1 mm/min	2990 MPa 2500 MPa	ASTM D638 ISO 527
Flexural Stress	75 MPa	ASTM D790
Flexural Stress	66 MPa	ISO 178
Flexural Modulus	2810 MPa	ASTM D790
Flexural Modulus	2500 MPa	ISO 178

Thermal	Nominal Value	Test Method
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa	97 °C 87 °C	ASTM D648
CTE, Flow -40 - 40 °C -40 - 40 °C	7.9e-05 1/°C 7.8E-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40 - 40 °C -40 - 40 °C	7.6E-05 1/°C 9.6E-05 1/°C	ASTM E831 ISO 11359-2
HDT/Bf(0.45)	91 °C	ISO 75/Bf
HDT/Af(1.8)	78 °C	ISO 75/Af
Electrical	Nominal Value	Test Method
Volume Resistivity	100 - 1.0E+06 ohms·cm	ASTM D257
Surface Resistivity	10 - 1.0E+05 ohms	ASTM D257
Shielding Effectivness @ 3Mm	40 - 55 dB	SABIC Method
Processing		Nominal Value
Drying Temperature<Injection>		80 °C
Drying Time<Injection>		4 hrs
Maximum Moisture Content<Injection>		0.05 - 0.1 %
Melt Temperature<Injection>		240 - 255 °C
Front, Zone 3 Temperature<Injection>		255 - 265 °C
Middle, Zone 2 Temperature<Injection>		230 - 245 °C
Rear, Zone 1 Temperature<Injection>		210 - 220 °C
Mold Temperature<Injection>		70 - 95 °C
Back Pressure<Injection>		0.2 - 0.3 MPa
Screw Speed<Injection>		30 - 60 rpm

Product Description
A semi-conductive grade of acetal copolymer for applications requiring rapid dissipation of static build- up.Information provided by Celanese Corporation.
General
Form	Resin	Pellets
Physical			Nominal Value	Test Method
Density / Specific Gravity			1.40 g/cm³
Water Absorption			0.21 %	ASTM D570
Moisture Absorption at Equilibrium			0.80 %	ASTM D570
Linear Mold Shrinkage			2.2 %
Linear Mold Shrinkage, Transverse			1.8 %
Hardness, Rockwell R			111	ASTM D785
Mechanical			Nominal Value	Test Method
Tensile Strength, Yield			37.0 MPa	ASTM D638
Elongation at Break			30 %	ASTM D638
Flexural Strength			52.0 MPa	ASTM D790
Flexural Modulus			2100 MPa	ASTM D790
Compressive Strength			66.0 MPa	ASTM D695
Shear Strength			40.0 MPa	ASTM D732
Izod Impact, Notched Temperature; 23 °C Temperature; -29 °C			50 J/m 30 J/m	ASTM D256
Thermal			Nominal Value	Test Method
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa			152 °C 106 °C	ASTM D648
Flammability, UL94			HB	UL 94