A234 WP1 WP5 WP11 WP 22 WP9 WP91 Alloy Fittings
Size 1/2"TO 24"(seamless), 26" TO 48" (welded)
Pressure SCH 5S TO SCH 160, XXS
Connection Butt Welding
Standard ANSI, JIS, DIN, EN, ISO, GB, SH AND HG
Packing wooden cases or customerized
Production Capacity 1000 Tons per month
Product Range: 45, 90, 180 degree,2D,3D,4D,5D,6D.......
Standard: ASTM A234
Material:; WP1 WP5 WP9 WP11 WP12 WP22 WP91
1. Chemical Composition Requirements
| Chemical Composition of ASTM A234 Alloy Steel Pipe Fittings(%) |
| Grade |
C |
Mn |
P |
S |
Si |
Cr |
Mo |
Others |
| WP1 |
0.28 |
0.30-0.90 |
0.045 |
0.045 |
0.10-0.50 |
- |
0.44-0.65 |
- |
| WP12 CL1, WP12 CL2 |
0.05-0.20 |
0.30-0.80 |
0.045 |
0.045 |
0.60 |
0.80-1.25 |
0.44-0.65 |
- |
| WP11 CL1 |
0.05-0.15 |
0.30-0.60 |
0.030 |
0.030 |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
- |
| WP11 CL2, WP11 CL3 |
0.05-0.20 |
0.30-0.80 |
0.040 |
0.040 |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
- |
| WP22 CL1, WP22 CL3 |
0.05-0.15 |
0.30-0.60 |
0.040 |
0.040 |
0.50 |
1.90-2.60 |
0.87-1.13 |
- |
| WP24 |
0.05-0.10 |
0.30-0.70 |
0.020 |
0.010 |
0.15-0.45 |
2.20-2.60 |
0.90-1.10 |
*A |
| WP5 CL1, WP5 CL3 |
0.15 |
0.30-0.60 |
0.040 |
0.030 |
0.50 |
4.0-6.0 |
0.44-0.65 |
- |
| WP9 CL1, WP9 CL3 |
0.15 |
0.30-0.60 |
0.030 |
0.030 |
1.00 |
8.0-10.0 |
0.90-1.10 |
- |
| WPR |
0.20 |
0.40-1.06 |
0.045 |
0.050 |
- |
- |
- |
*B |
| WP91 |
0.08-0.12 |
0.30-0.60 |
0.020 |
0.010 |
0.20-0.50 |
0.85-1.05 |
0.85-1.05 |
*C |
| WP911 |
0.09-0.13 |
0.30-0.60 |
0.020 |
0.010 |
0.10-0.50 |
0.90-1.10 |
0.90-1.10 |
*D |
| WP92 |
0.07-0.13 |
0.30-0.60 |
0.020 |
0.010 |
0.50 |
0.30-0.60 |
0.30-0.60 |
*E |
*All values listed are maximum unless a range is provided or otherwise specified.
*A - Cu:0.75-1.25,Al:≤0.020,B:0.0015-0.0070,N:≤0.12,Ti:0.06-0.10,V:0.20-0.30. *B - Ni:1.60-2.24,Cu:0.75-1.25.
*C - Ni:≤0.40,V:0.18-0.25,Co:0.06-0.10,N:0.03-0.07,Al:≤0.02,Ti:≤0.01,Zr:≤0.01.
*D - Ni:≤0.40,V:0.18-0.25,Co:0.06-0.10,N:0.04-0.09,Al:≤0.02,B:0.003-0.006,W:0.90-1.10,Ti:≤0.01,Zr:≤0.01.
*E - Ni:≤0.40,Al:≤0.02,B:0.001-0.006,Co:0.04-0.09,N:0.03-0.07,Ti:≤0.01,W:1.50-2.00,V:0.15-0.25,Zr:≤0.01.
*The unit [%" shall be applied to the chemical composition values from *A to *E.
2. Mechanical Properties
| Mechanical Properties of ASTM A234 Alloy Steel Pipe Fittings |
| Grade |
Tensile Strength, min. ksi[MPa] |
Yield Strength, min. ksi[MPa] |
Elongation, min. % |
| Longitudinal |
Transverse |
| WP1 |
55-80[380-550] |
30[205] |
20 |
13 |
| WP12 CL1 |
60[415] |
32[220] |
22 |
14 |
| WP12 CL2 |
70[485] |
40[275] |
22 |
14 |
| WP11 CL1 |
60[415] |
30[205] |
22 |
14 |
| WP11 CL2 |
70[485] |
40[275] |
22 |
14 |
| WP11 CL3 |
75[520] |
45[310] |
22 |
14 |
| WP22 CL1 |
60[415] |
30[205] |
22 |
14 |
| WP22 CL3 |
75[520] |
45[310] |
22 |
14 |
| WP24 |
85[585] |
60[415] |
20 |
- |
| WP5 CL1 |
60[415] |
30[205] |
22 |
14 |
| WP5 CL3 |
75[520] |
45[310] |
22 |
14 |
| WP9 CL1 |
60[415] |
30[205] |
22 |
14 |
| WP9 CL3 |
75[520] |
45[310] |
22 |
14 |
| WPR |
63-99[435-605] |
46[315] |
20 |
- |
| WP91 |
90[620] |
60[415] |
20 |
13 |
| WP911 |
90-120[620-840] |
64[440] |
20 |
13 |
| WP92 |
90-120[620-840] |
64[440] |
20 |
13 |
3. Heat Treatment
Pipe fittings of ASTM A234 alloy steel, after forming at an elevated temperature, shall be cooled to a temperature. below the critical range under suitable conditions to prevent injurious defects caused by too rapid cooling, but in no case more rapidly than the cooling rate in still air.
- Fittings of Grades WP1, WP11 Class 1, WP11 Class 2, WP11 Class 3, WP12 Class 1, WP12 Class 2, WP22 Class 1, WP22 Class 3, WP5, and WP9 shall be furnished in the full-annealed, isothermal-annealed, or normalized and tempered condition. If normalized and tempered, the tempering temperature for WP11 Class 1, WP11 Class 2, WP11 Class 3, WP12 Class 1, and WP12 Class 2 shall not be less than 1150 °F [620 °C]; for Grades WP5, WP9, WP22 Class 1, and WP22 Class 3 the tempering temperature shall not be less than 1250 °F [675 °C].
- Fittings of Grades WP1, WP12 Class 1, or WP12 Class 2 either hot formed or cold formed may be given a final heat treatment at 1200 °F [650 °C].
- Fittings of WP24 either hot formed or cold formed shall be furnished in the normalized and tempered condition. The normalizing temperature range shall be 1800 to 1975 °F [980 to 1080 °C]. The tempering temperature range shall be 1350 to 1470 °F [730 to 800 °C].
- Fittings in all thicknesses produced by fusion welding after the heat treatment specified in 1 shall be post-weld heat treated at a temperature not less than prescribed above for tempering except that Grade WP1 is required to be post-weld heat treated only when the nominal wall thickness at the welded joint is 1⁄2 in. [13 mm] or greater, and except that preheat and post weld heat treatment are not required for WP24 fittings whose section thickness does not exceed 0.500 in. [12.7 mm].
- Grade WP91 shall be normalized at 1900 °F [1040 °C] minimum, and 1975 °F [1080 °C] maximum, and tempered in the temperature range of 1350 °F [730 °C] to 1470 °F [800 °C] as a final heat treatment.
- Grade WP911 shall be normalized in the temperature range of 1900 to 1975 °F [1040 to 1080 °C], and tempered in the temperature range of 1365 to 1435 °F [740 to 780 °C] as a final heat treatment.
- Grade WP92 shall be normalized at 1900 °F [1040 °C] minimum, and 1975 °F [1080 °C] maximum, and tempered in the temperature range of 1350 °F [730 °C] to 1470 °F [800 °C] as a final heat treatment.