| Material: | Polypropylene/PP |
|---|---|
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Film Pressure |
| Color: | White |
| Application: | for Extrusion |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
| Performance | Test conditions [state] | Test data | Data unit |
| Density | 0.9 | g/m3 | |
| Melt flow rate | 10 | g/10min | |
| Tensile yield strength | 25 | Mpa | |
| Elongation at break | ≥600 | % | |
| Notch impact strength | 23ºC | 8 | kj/m2 |
| Flexural modulus | ≥1000 | Mpa | |
| Rockwell hardness | 90 | R | |
| Load heat distortion temperature | 80 | ºC |
| Item | Test method | Test data | Data unit | |
| Density | ASTM D-792 | 0.905 | g/cm3 | |
| MFR | ASTM D-1238 | 3.5 | g/10min | |
| Tensile yield strength | ASTM D-638 | 23 | Mpa | |
| The yield tensile elongation | ASTM D-638 | 10 | % | |
| Rockwell hardness | ASTM D-785 | 80 | % | |
| notched izod impact strength | -20ºC | ASTM D-256 | 100 | J |
| 23ºC | ASTM D-256 | 750 | J/m | |
| Flexural modulus | ASTM D-790A | 1000 | Mpa | |
| HDT | ASTM D-648 | 85 | ºC | |
| Vicat Softening Temperature | ASTM D-1525B | 145 | ºC | |
| Item | Test method | Test data | Data unit | ||
| MFR | GB/T 3682-2000 | 3.19 | g/10min | ||
Mould Shrinkage |
Parallel |
GB/T 17037.4-2003 | 1.6 | % | |
| Vertical |
GB/T 17037.4-2003 | 1.7 | % | ||
| Flexural Modulus | GB/T 9341-2000 | 1105 | Mpa | ||
| Tensile yield stress | GB/T 1040.2-2006 | 23 | Mpa | ||
| Charpy Notched Impact Strength |
-20ºC | GB/T 1043-2008 | 8.4 | KJ/m2 | |
| 23ºC | GB/T 1043-2008 | 20 | KJ/m2 | ||
| Rockwell hardness | GB/T 3398.2-2008 | 87 | |||
| HDT | GB/T 1634.1-2004 | 76 | ºC | ||
| Ash content |
GB/T 9345.1-2008 | 0.011 | % | ||