Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060) pictures & photos

Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Raw Material:	Silicone Raw Material
Material:	Silicone Rubber
Appearance:	Liquid
Form:	Liquid Rubber
Item:	Mcsil-L30
Color:	off-White

Samples:	US$ 1/Piece 1 Piece(Min.Order) \| Request Sample

Customization:	Available \| Customized Request

Contact Supplier

Contact Now

Inquiry Basket

Mingcheng Group Limited

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Product Description

Company Info.

Basic Info.

Model NO.

MCSIL2010-2060 Silicone rubber

Mixing Ratio

100:5

Mixed Viscosity

16700 Cps

Working Time

60-80 Mins

Curing Time

8-12 Hours

Hardness

28-30 Shore a

Tear Strength

28 N/Mm

Tensile Strength

4 Mpa

Elongation at Break

510%

Transport Package

20kg/Drum, 25kg/Drum or 200kg/Drum

Specification

REACH, MSDS, SGS

Trademark

MC SILICONE

Origin

Dongguan, China

HS Code

39100000

Production Capacity

4000kg/Day

Product Description

Description of Tin Base Mold Making Silicone

RTV2 Tin-based silicones, also called condensation cure silicone, are two- component materials which can cure at room temperature to flexible, high tear-strength rubbers. Tin cured silicone can be poured onto models or they can be made brushed by adding a thixotropic additive. They are ideal for molds where easy release or high temperature resistance (Max 200 C) is required.

Characteristics of Tin Base Mold Making Silicone

Tin cure silicone rubber for molding is white or translucent flowing liquid with general hardness of 15-60shore A after curing. Molding silicone rubber is a kind elastic silicone rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation, Stripping the gender is good, Linear shrinkage rate low, Size stability is good.
Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Applications of Tin Base Mold Making Silicone

Tin cured silicone can be used for casting polyurethane, epoxy, polyester resin, PU resin, cement, plaster, gypsum, candle, soap, waxes, toys crafts, poly resin crafts, Lighting, plastic toys, stationery gifts, statue, relieve furniture, furniture decorative materials, artificial stone, building decoration material, sculpture, sandstone, low melt alloys/metals, urethane and so on.
Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

One Datasheet of Tin Base Mold Making Silicone

Item MCSIL-L30
Coloroff-white
Curing agentCA30
Mixing ratio100: 5
Mixed viscosity16700 cps
Working time 60-80 mins
Curing time 8-12 Hours
Hardness28-30 Shore A
Tear Strength28 N/mm
Tensile Strength4 Mpa
Shrinkage≤ 0.3%
Relative density 1.1-1.15 g/cm3
Elongation at break510%

Instructions for Making Silicone Molds

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Packing of Tin Base Mold Making Silicone

20kg/plastic drum, 25kg/plastic drum, 25kg/steel drum or 200kg/drum
Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Need more information, please feel free to contact Julie for further discussion.

Item	MCSIL-L30
Color	off-white
Curing agent	CA30
Mixing ratio	100:5
Mixed viscosity	16700 cps
Working time	60-80 mins
Curing time	8-12 Hours
Hardness	28-30 Shore A
Tear Strength	28 N/mm
Tensile Strength	4 Mpa
Shrinkage	≤0.3%
Relative density	1.1-1.15 g/cm3
Elongation at break	510%

Send your message to this supplier

*From:

*To:

*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for?  Post a Sourcing Request Now

Find Similar Products By Category

Supplier Homepage Products Condensation Cure(Tin Based) Silicones Others Condensation Cure(Tin Based) Silicones Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Hot Searches

Silicone Rubber bulkbuy

Product Groups

More Product Catalogs

Contact Supplier

Contact Now

Inquiry Basket

Mingcheng Group Limited

Gold Member Since 2013

Suppliers with verified business licenses

Manufacturer/Factory

Terms of Payment

LC, T/T, D/P, PayPal, Western Union, Small-amount payment, Money Gram

OEM/ODM Availability

Yes

Condensation Cured Tin Base Mold Making RTV-2 Liquid Silicone (MCSIL2010-2060)

Contact Supplier

Product Description

Company Info.

Basic Info.

Product Description

Send your message to this supplier

Find Similar Products By Category

Hot Searches

You Might Also Like

Product Groups

Contact Supplier