| Material: | Acrylic |
|---|---|
| Kind: | Color Plastic Sheet |
| Water Absorption: | 0.1%~0.3% |
| Contraction Percentage: | ＜0.4% |
| Tensile Strength: | 81~130MPa |
| Thickness: | 2mm, 3mm, 4mm, up to 60mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
|
Material
|
100% virgin Mitsubishi material
|
|
Thickness
|
1.8, 2, 3, 4, 5, 8,10,15,20, 30, 50,60mm (1.8-60mm)
|
|
Color
|
transparent, white, opal, black, red, green, blue, yellow, etc. OEM color OK
|
|
Standard size
|
1220*1830, 1220*2440,1270*2490, 1610*2550, 1440*2940, 1850*2450, 1050*2050,1350*2000,2050*3050,1220*3050 mm |
|
Certificate
|
CE, SGS, DE, and ISO 9001
|
|
Equipment
|
Imported glass models (from Pilkington Glass in U. K. )
|
|
MOQ
|
2 tons, can be mixed with colors/sizes/thickness
|
|
Delivery
|
10-25 days
|
|
|
PROPERTY
|
UNIT
|
VALUE
|
|
MECHANICAL
|
Specific Gravity
|
-
|
1.19-1.2
|
|
Roswell Hardness
|
kg/cm 2
|
M-100
|
|
|
Shear Strength
|
kg/cm 2
|
630
|
|
|
Flexural Strength
|
kg/cm 2
|
1050
|
|
|
Tensile Strength
|
kg/cm 2
|
760
|
|
|
Compressive Strength
|
kg/cm 2
|
1260
|
|
|
ELECTRICAL
|
Didlectic Strength
|
Kv/mm
|
20
|
|
Surface Resistivity
|
Ohm
|
> 10 16
|
|
|
OPTICAL
|
Light Transmittance
|
%
|
93
|
|
Refractive Index
|
-
|
|
|
|
THERMAL
|
Specific Heat
|
Cal/grºC
|
0.35
|
|
Coefficient of Thermal Cortductivily
|
Cal/xee/cm/ºC/cm
|
|
|
|
Hot Forming Temp
|
ºC
|
140-180
|
|
|
Hot Defomation Temp
|
ºC
|
100
|
|
|
Thermal Expansion Coefficient
|
Cmfcm/V
|
6×10-5
|
|
|
MISCELLANEOUS
|
Water Absorption(24Hrs)
|
%
|
0.3
|
|
Teste
|
%
|
None
|
|
|
Odor
|
|
|
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}