| Type: | Graphite Sheets |
|---|---|
| Composition: | Graphite |
| Carbon Content: | Medium-Carbon |
| Grade: | Industrial Grade |
| Forming Way: | Grinding |
| Crystal Morphology: | Compact Crystalline Graphite |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
Graphite Block/High Density Graphite Block/Isostatic Graphite | Item | Unit | Grade | |||||
| Grain Size | mm | 0.8 | 0.8 | 2 | 2 | 4 | |
| Bulk Density | g/cm³ | ≥ 1.73 | ≥ 1.70 | ≥ 1.60 | ≥ 1.60 | ≥ 1.60 | |
| Specific Resistance | µΩ.m | ≤ 8.0 | ≤ 8.5 | ≤ 8.5 | ≤ 9.0 | ≤ 9.0 | |
| Flexural strength | Mpa | ≥ 20.5 | ≥ 13.0 | ≥ 13.0 | ≥ 7.8 | ≥ 7.8 | |
| Compressive Strength | Mpa | ≥ 40.0 | ≥ 30.0 | ≥ 30.0 | ≥ 20.0 | ≥ 20.0 | |
| C.T.E(100 Dregree)ºC | 10-6/°C | ≤ 2.3 | ≤ 2.3 | ≤ 2.3 | ≤ 2.3 | ≤ 2.3 | |
| Model | / | XS-7 | XS-8 | XS-6 | H10(EDM) | H5(EDM) |
| Bulk Dengsity | g/cm³ | 1.85 | 1.91 | 1.90 | 1.78 | 1.68 |
| Specific Resistance | µΩ.m | 11-13 | 11-13 | 8-9 | 9-10 | 13 |
| Flexrual Strength | Mpa | 51 | 50 | 55 | 43 | 38 |
| Compressive Strength | Mpa | 115 | 135 | 95 | 85 | 86 |
| Thermal Conductivity | W/(m.k) | 85 | 85 | 140 | 110 | 90 |
| Shore Hardness | HSD | 65 | 70 | 53 | 56 | 51 |
| C.T.E(100-600)°C | 10-6/°C | 5.6 | 5.85 | 5.1 | 5.5 | 5 |
| Ash | PPM | 500 | 500 | 500 | 500 | 500 |
| Model | / | JS-5 | JS-4 |
| Bulk Dengsity | g/cm³ | 1.85 | 1.80 |
| Specific Resistance | µΩ.m | 8.5 | 8.5 |
| Flexrual Strength | Mpa | 46 | 38 |
| Conpressive Strength | Mpa | 85 | 65 |
| Thermal Conductivity | W/(m.k) | 139.2 | 121.1 |
| Shore Hardness | HSD | 48 | 42 |
| C.T.E(Indoor 600°C) | 10-6/°C | 4.75 | 5.46 |
| Ash | PPM | 500 | 500 |
Packaging Details Plywood box packing , foam board filling up interspace.
Application:
Foundry, metallurgy, various high temperature industrial furnaces, glass, chemical, mechanics, electronics etc.WE havea large customers from international market .