general electric potting silicone rubber material
general electric potting silicone rubber Product Feature
HY 9055 is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate),PP,ABS,PVC, etc. and metal materials.
general electric potting silicone rubber Typical Application
HY 9055 could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
general electric potting silicone rubber TECHNICAL GUIDELINES
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100°C, the silicone will cure in 15 minutes; while in 25°C room temperature, the silicone will cure around 8 hours.
general electric potting silicone rubber Notes:
1.The following material may hinder the curing of HY 9055, So pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin;
Sulphur, sulfide and sulfur rubber materials;
Amine compounds as well as contains the amine materials;
Pewters solder flux;
2. HY 9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
3. HY 9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.
black / transparent / white
Mixing ratio (%)
Pot life(25°C) (mins)
20 - 30
Curing time (mins)
2 - 4
Hardness shore A
15 ± 2
Tensile strength (Mpa)
0.5 - 1.5
Elongation at break (%)
30 - 50
Dielectric strength (kv/m-1)
Specific inductive capacity(1MHz)
2.8 - 3.2
Breakdown voltage (KV.mm-1)
Volume resistivity (Ω)
Dielectric loss factor (1MHz)